effects of maleic anhydride and glycidyl methacrylate on morphological and physical properties of styrene wood-polymer
نویسندگان
چکیده
the current research was planned to investigate the effect of maleic anhydride (man) and glycidyl methacrylate (gma) treatments on morphological and physical properties of the hornbeam wood-styrene composite. test samples were divided according to astm d4446-05 to control and treated with man, st, man/st and man /st/gma. treatment was performed by vacuum- pressure method using a experimental cylinder. the presence of styrene in the cell cavities, swelling of treated wood with man and interaction between man/st and man/st/gma with wood cell wall were confirmed by scanning electron microscopy. according to the results, density and weight of the specimens were increased as 73.47 and 79.91; and 5.95 and 11.9% by addition of man and man/gma, respectively. strong interactions between wood structure and combination of man/st/gma led toan improvement in the compatibility of polymer with cell wall and reduction in porosity of the treated wood. hydrophobicity and dimensional stability of wood polymer composites were improved as the result of modification with man and impregnation with st, so that after the longest immersion time, water absorption and dimensional changes in man/st/gma with 42/44% weight percent gain, decreased up to 57/78 and 50.15% in comparison with the untreated samples. the highest anti-swelling efficiency was determined in man/st/gma treatment.
منابع مشابه
Effect of Styrene Maleic Anhydride on Physical and Mechanical Properties of Recycled Polystyrene Wood Flour Composites
In this work, the influence of three types of styrene maleic anhydride (SMA) oligomers on the adhesion of polystyrene wood plastic composites (WPC) was investigated. The composites were processed on a twin-screw co-rotating extruder below 200°C using 20 wt% of wood flour. The styrene maleic anhydride with different content of maleic anhydride groups, 30%, 25% and 20% (w/w) and levels of 1, 2 an...
متن کاملClay Dispersed Styrene-co-Glycidyl Methacrylate Impregnated Kumpang Wood Polymer Nanocomposites: Impact on Mechanical and Morphological Properties
Physical, mechanical, and morphological properties of a clay dispersed styrene-co-glycidal methacrylate (ST-co-GMA) impregnated wood polymer nanocomposite (WPNC) were evaluated. The WPNC was characterized by Fourier transform infrared spectroscopy (FTIR), scanning electron microscopy (SEM), 3-point bending, free-vibration testing, and Xray diffraction (XRD) measurements. The FT-IR results showe...
متن کاملdetermination of some physical and mechanical properties red bean
چکیده: در این تحقیق، برخی خواص فیزیکی و مکانیکی لوبیا قرمز به-صورت تابعی از محتوی رطوبت بررسی شد. نتایج نشان داد که رطوبت بر خواص فیزیکی لوبیا قرمز شامل طول، عرض، ضخامت، قطر متوسط هندسی، قطر متوسط حسابی، سطح تصویر شده، حجم، چگالی توده، تخلخل، وزن هزار دانه و زاویه ی استقرار استاتیکی در سطح احتمال 1 درصد اثر معنی داری دارد. به طوری که با افزایش رطوبت از 54/7 به 12 درصد بر پایه خشک طول، عرض، ضخام...
15 صفحه اولthe effects of planning on accuracy and complexity of iranian efl students’ written narrative task performance
this study compared the different effects of form-focused guided planning vs. meaning-focused guided planning on iranian pre-intermediate students’ task performance. the study lasted for three weeks and concentrated on eight english structures. forty five pre-intermediate iranian students were randomly assigned to three groups of guided planning focus-on-form group (gpfg), guided planning focus...
15 صفحه اولthe effects of previewing and providing background knowledge on iranian university efl learners’ comprehension of literary and academic texts
abstract poor reading comprehension can result in failure in using references, benefiting from professional gatherings and resources, keeping up with the growing body of knowledge in the virtual world of the internet, and failing to achieve in efl programs. the purpose of the present quasi-experimental study was to explore the effects of background knowledge and previewing narrative and expos...
15 صفحه اولFabrication and Characterization of Proton Conductive Membranes Based on Poly(methyl methacrylate-co-maleic anhydride)
In this study, proton conductive composite membranes were produced by using a poly(methylmethacrylate-co-maleic anhydride) (P(MMA-co-MAH)) copolymer and phosphotungstic Acid (PWA) as an additive of the proton conductive agent. P(MMA/MAH) 70/30, 50/50, and 30/70 were synthesized using a free radical polymerization reaction. PWA with a concentration of 2% was added to...
متن کاملمنابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
عنوان ژورنال:
جنگل و فرآورده های چوبجلد ۶۹، شماره ۲، صفحات ۳۶۱-۳۷۴
کلمات کلیدی
میزبانی شده توسط پلتفرم ابری doprax.com
copyright © 2015-2023