synthesis of zro2 nanoparticle by combination of sol-gel auto-combustion method- irradiation technique, and preparation of al-zro2 metal matrix composites

نویسندگان

s. a. khorramie

department of chemistry, north tehran branch, islamic azad university, tehran, iran. m. a. baghchesara

department of metallurgy & materials engineering, masjed soleyman branch, islamic azad university, masjed soleyman, iran. r. lotfi

department of chemistry, north tehran branch, islamic azad university, tehran, iran. sh. moradi dehagi

department of chemistry, north tehran branch, islamic azad university, tehran, iran.

چکیده

nanocrystalline zro2 with particle size of about 38 nm was directly synthesized by sol-gel auto-combustion method. the overall process involved three steps: formation of homogeneous sol at 50-55°c; formation of dried gel at 110°c, and combustion of the dried gel at 400°c. experiments revealed that zro2 dried gel derived from glycine (fuel) and nitrate sol exhibited self propagating combustion at 400°c  that  it was ignited in air. the auto-combustion was considered as a heat-induced exothermic oxidation-reduction reaction between nitrate ions and carboxyl group. after auto-combustion, products were calcined at 650°c. zro2 nano particle were incorporated into the a356 aluminum alloy by a mechanical stirred at 850°c and after that, cylindrical specimens were cast. after preparing the samples, mechanical properties were measured. the results of microstructure, compression and hardness tests indicated that addition of zro2 nano particulates to aluminum matrix composites improved the mechanical properties. also, based on experiments, it was revealed that the presence of zro2 reinforcement    led to significant improvement in hardness and compressive strength.

برای دانلود باید عضویت طلایی داشته باشید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

Synthesis of ZrO2 nanoparticle by combination of sol-gel auto-combustion method- irradiation technique, and preparation of Al-ZrO2 metal matrix composites

Nanocrystalline ZrO2 with particle size of about 38 nm was directly synthesized by sol-gel auto-combustion method. The overall process involved three steps: formation of homogeneous sol at 50-55°C; formation of dried gel at 110°C, and combustion of the dried gel at 400°C. Experiments revealed that ZrO2 dried gel derived from glycine (Fuel) and nitrate sol exhibited self pr...

متن کامل

Synthesis of ZrO2 nanoparticle by combination of sol-gel auto-combustion method- irradiation technique, and preparation of Al-ZrO2 metal matrix composites

Nanocrystalline ZrO2 with particle size of about 38 nm was directly synthesized by sol-gel auto-combustion method. The overall process involved three steps: formation of homogeneous sol at 50-55°C; formation of dried gel at 110°C, and combustion of the dried gel at 400°C. Experiments revealed that ZrO2 dried gel derived from glycine (Fuel) and nitrate sol exhibited self pr...

متن کامل

Preparation and Evaluation of NiFe204 and CuFe204 Nanoeatalysts by Combination of Sol- Gel Auto-Combustion Method and Irradiation Technique

The dried nitrate-urea gels exhibit the combination of autoicatatric combustion behavior and ultrasonic, whichcan be used to synthesize the nanocatalyst ferrite powders. Cu and Ni Unites nanocatalyst powders sithcomposition of Caned], and NiFe204 were synthesized by a sol-gel auto catalnic combustion process. Themolar ratio between metal ions and urea was 11.2. The sob gel process was done at 8...

متن کامل

preparation and evaluation of nife204 and cufe204 nanoeatalysts by combination of sol- gel auto-combustion method and irradiation technique

the dried nitrate-urea gels exhibit the combination of autoicatatric combustion behavior and ultrasonic, whichcan be used to synthesize the nanocatalyst ferrite powders. cu and ni unites nanocatalyst powders sithcomposition of caned], and nife204 were synthesized by a sol-gel auto catalnic combustion process. themolar ratio between metal ions and urea was 11.2. the sob gel process was done at 8...

متن کامل

Preparation and Characterization of ZrO2/TiO2 Nanocomposite under Ultrasonic Irradiation by Sol-gel Route

TiO2/ZrO2 nanocomposite was obtained by the sonochemical technique. In this method, two separate gels containing zirconium and titanium were prepared and mixed together. The precursor sol of zirconium was prepared from an aqueous solution of ZrCl4. The precursor titanium tetra isopropoxide (TTIP) dissolved in isopropanol. Mixing of Titanium and Zirconium gels was resulted in a yellow TiO2/ZrO2 ...

متن کامل

Preparation and Characterization of ZrO2/TiO2 Nanocomposite under Ultrasonic Irradiation by Sol-gel Route

TiO2/ZrO2 nanocomposite was obtained by the sonochemical technique. In this method, two separate gels containing zirconium and titanium were prepared and mixed together. The precursor sol of zirconium was prepared from an aqueous solution of ZrCl4. The precursor titanium tetra isopropoxide (TTIP) dissolved in isopropanol. Mixing of Titanium and Zirconium gels was resulted in a yellow TiO2/ZrO2 ...

متن کامل

منابع من

با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید


عنوان ژورنال:
international journal of nano dimension

جلد ۲، شماره ۴، صفحات ۲۶۱-۲۶۷

میزبانی شده توسط پلتفرم ابری doprax.com

copyright © 2015-2023