sono-synthesis and characterization of zro2/zno nanocomposite, composition effect on enhancing of photocatalytic properties

نویسندگان

sh. aghabeygi

department of chemistry, islamic azad university, east tehran branch, qiamdasht, tehran, iran. m. zare-dehnavi

department of chemistry, islamic azad university, east tehran branch, qiamdasht, tehran, iran.

چکیده

nanocomposite of zro2/zno was prepared under ultrasonic irradiation by sol gel process from directly mixing zirconium and zinc gels. the mixture was placed under ultrasonic irradiation for 2 hours. after the aging time and filtration of the reaction mixture, the filtrated composite gel was calcinated at 500 °c for 3h in furnace. the precursor gels of zirconium and zinc were prepared from dissolving of zrcl4 and zn(ch3coo)2.2h2o into deionized water(di). nano zno, nano zro2 and zro2/zno nanocomposite were characterized. the ft-ir analysis and the xrd study were exhibited that the crystal structure and purity of the zro2/zno nanocomposite fesem images were indicated the morphology and the average size of the nps. the average size of the nano zno, nano zro2 and zro2/zno nanocomposite were determined 54, 23and 37 nm respectively. the photocatalytic performance was increased when nanocomposite of zro2/zno was used to degradation of congo red (cr) solution. the zro2/zno nanocomposite was shown higher photo-degradation efficiency of congo red than of pure nano zro2 and nano zno.

برای دانلود باید عضویت طلایی داشته باشید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

Sono-Synthesis and characterization of ZrO2/ZnO nanocomposite, composition effect on enhancing of photocatalytic properties

Nanocomposite of ZrO2/ZnO was prepared under ultrasonic irradiation by sol gel process from directly mixing Zirconium and Zinc gels. The mixture was placed under ultrasonic irradiation for 2 hours. After the aging time and filtration of the reaction mixture, the filtrated composite gel was calcinated at 500 °C for 3h in furnace. The precursor gels of zirconium and zinc were prepared ...

متن کامل

Sono-Synthesis and characterization of ZrO2/ZnO nanocomposite, composition effect on enhancing of photocatalytic properties

Nanocomposite of ZrO2/ZnO was prepared under ultrasonic irradiation by sol gel process from directly mixing Zirconium and Zinc gels. The mixture was placed under ultrasonic irradiation for 2 hours. After the aging time and filtration of the reaction mixture, the filtrated composite gel was calcinated at 500 °C for 3h in furnace. The precursor gels of zirconium and zinc were prepared ...

متن کامل

synthesis and characterization of some macrocyclic schiff bases

ماکروسیکلهای شیف باز از اهمیت زیادی در شیمی آلی و دارویی برخوردار می باشند. این ماکروسیکلها با دارابودن گروه های مناسب در مکانهای مناسب می توانند فلزاتی مثل مس، نیکل و ... را در حفره های خود به دام انداخته، کمپلکسهای پایدار تولید نمایند. در این پایان نامه ابتدا یک دی آلدئید آروماتیک از گلیسیرین تهیه می شود و در مرحله بعدی واکنش با دی آمینهای آروماتیک و یا آلیفاتیک در رقتهای بسیار زیاد منجر به ت...

15 صفحه اول

effect of seed priming and irrigation regimes on yield,yield components and quality of safflowers cultivars

این مطالعه در سال 1386-87 در آزمایشگاه و مزرعه پژوهشی دانشگاه صنعتی اصفهان به منظور تعیین مناسب ترین تیمار بذری و ارزیابی اثر پرایمینگ بر روی سه رقم گلرنگ تحت سه رژیم آبیاری انجام گرفت. برخی از مطالعات اثرات سودمند پرایمینگ بذر را بر روی گیاهان مختلف بررسی کرده اند اما در حال حاضر اطلاعات کمی در مورد خصوصیات مربوط به جوانه زنی، مراحل نموی، عملکرد و خصوصیات کمی و کیفی بذور تیمار شده ژنوتیپ های م...

منابع من

با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید


عنوان ژورنال:
international journal of nano dimension

جلد ۶، شماره ۳، صفحات ۲۹۷-۳۰۴

میزبانی شده توسط پلتفرم ابری doprax.com

copyright © 2015-2023