poly (lactide-co-glycolide) nanofibers coated with collagen and nano-hydroxyapatite for bone tissue engineering
نویسندگان
چکیده
please cite this article as : tavakoli-darestani r, kazemian gh, emami m, kamrani-rad a. poly (lactide-co-glycolide) nanofibers coated with collagen and nano-hydroxyapatite for bone tissue engineering. novel biomed 2013;1:8-15. background: a combination of polymeric nanofibrous scaffold and bioactive materials is potentially useful in bone regeneration applications. materials and methods: in the present study, poly (lactide-co-glycolide) (plga) nanofibrous scaffolds, fabricated via electrospinning, were initially coated with type i collagen and then with nano-hydroxyapatite. the prepared scaffolds were then characterized using sem and their ability for bone regeneration was investigated in a rat critical size bone defect using digital mammography, multislice spiral-computed tomography (msct) imaging, and histological analysis. results: electrospun scaffolds had nanofibrous structure with homogenous distribution of n-ha on collagen-grafted plga. after 8 weeks of implantation, no sign of inflammation or complication was observed at the site of surgery. according to digital mammography and msct, plga nanofibers coated simultaneously with collagen and ha showed the highest regeneration in rat calvarium. in addition, no significant difference was observed in bone repair in the group which received plga and the untreated control. this amount was lower than that observed in the group implanted with collagen-coated plga. histological studies confirmed these data and showed osteointegration to the surrounding tissue. conclusion: taking all together, it was demonstrated that nanofibrous structures can be used as appropriate support for tissue-engineered scaffolds, and coating them with bioactive materials will provide ideal synthetic grafts. fabricated plga coated with type i collagen and ha can be used as new bone graft substitutes in orthopaedic surgery and is capable of enhancing bone regeneration via characteristics such as osteoconductivity and osteointegration
منابع مشابه
Poly(lactide-co-glycolide)/hydroxyapatite nanofibrous scaffolds fabricated by electrospinning for bone tissue engineering.
Poly(lactide-co-glycolide) (PLGA) nanofibrous composite scaffolds having nano-hydroxyapatite particles (HAp) in the fibers were prepared by electrospinning of PLGA and HAp with an average diameter of 266.6 ± 7.3 nm. Microscopy and spectroscopy characterizations confirmed integration of the crystalline HAp in the scaffolds. Agglomerates gradually appeared and increased on the fiber surface along...
متن کاملGelatin Tight-Coated Poly(lactide-co-glycolide) Scaffold Incorporating rhBMP-2 for Bone Tissue Engineering
Surface coating is the simplest surface modification. However, bioactive molecules can not spread well on the commonly used polylactone-type skeletons; thus, the surface coatings of biomolecules are typically unstable due to the weak interaction between the polymer and the bioactive molecules. In this study, a special type of poly(lactide-co-glycolide) (PLGA)-based scaffold with a loosened skel...
متن کاملChitosan/poly(DL,lactide-co-glycolide) scaffolds for tissue engineering.
Chitosan/poly(DL-lactide-co-glycolide) (Ch/DL PLG) composite scaffolds were fabricated by freeze-drying lyophilization, and were evaluated and compared for use as a bone regeneration scaffold through measurements of the compression mechanical properties of the porous scaffolds. Also, In vitro cell culture of Sprague-Dawley rat's osteoblasts were used to evaluate the phenotype expression of cell...
متن کاملCollagen-Coated Poly(lactide-co-glycolide)/Hydroxyapatite Scaffold Incorporated with DGEA Peptide for Synergistic Repair of Skull Defect
The treatment of large-area bone defects remains a challenge; however, various strategies have been developed to improve the performances of scaffolds in bone tissue engineering. In this study, poly(lactide-co-glycolide)/hydroxyapatite (PLGA/HA) scaffold was coated with Asp-Gly-Glu-Ala (DGEA)-incorporated collagen for the repair of rat skull defect. Our results indicated that the mechanical str...
متن کاملPoly(lactide-co-glycolide)/titania composite microsphere-sintered scaffolds for bone tissue engineering applications.
The objective of this study was to synthesize and characterize novel three-dimensional porous scaffolds made of poly(lactic-co-glycolic acid) (PLGA)/nano-TiO(2)-particle composite microspheres for potential bone repair applications. The introduction of TiO(2) component has been proven capable of largely enhancing mechanical properties of PLGA/TiO(2) microsphere-sintered scaffold ("PLGA/TiO(2)-S...
متن کاملمنابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
عنوان ژورنال:
novelty in biomedicineجلد ۱، شماره ۱، صفحات ۸-۱۵
کلمات کلیدی
میزبانی شده توسط پلتفرم ابری doprax.com
copyright © 2015-2023