comparison of chlorhexidine 2% and sodium hypochlorite 5% as rewetting agents on resin- dentin micro tensile bond strength
نویسندگان
چکیده
resin- dentin interface hydrolysis is one of the greatest problems in restorative dentistry, because of collagenolytic and proteolytic activity of dentin enzymes. the aim of this study was to compare the effect of chx 2% and naocl 5% as rewetting agent on resin-dentin micro tensile bond strength.methods: 45 extracted, human caries-free third molar teeth were collected. after exposing of superficial dentin, etching and rinsing of dentin were done. specimens were divided into 3 equal groups. in group 1, after drying of dentin, chx 2% was used as rewetting agent for 60 seconds. in group2, naocl 5% used as rewetting agent for 120 sec and in group 3 (control), blot dry technique with water was used for substrate. adhesive system (singlebond , 3m espe , usa) and composite build up (filtek z250 ,3m espe , usa)) were applied for all groups. after 6 month storage, μtbs measured for hourglass-shaped specimens. specimens loaded for micro tensile bond strength until fracture occurred. results: micro tensile bond strength of group 1 significantly was higher than other groups (52.67±6.862). there was no significant difference between group 2(18.59 ± 6.081) and group 3(28.84± 6.231). (p= 0.094). conclusion: chx acts as matrix metalloproteinases inhibitor and by preventing dentin collagen degradation can preserve the bond strength after 6 months.
منابع مشابه
Comparison Of Chlorhexidine 2% And Sodium Hypochlorite 5% As Rewetting Agents On Resin- Dentin Micro Tensile Bond Strength
Resin- dentin interface hydrolysis is one of the greatest problems in restorative dentistry, Because of collagenolytic and proteolytic activity of dentin enzymes. The aim of this study was to compare the effect of CHX 2% and NaOCl 5% as rewetting agent on resin-dentin micro tensile bond strength.Methods: 45 extracted, human caries-free third molar teeth were collected. After exposing of superfi...
متن کاملImmediate and delayed micro-tensile bond strength of different luting resin cements to different regional dentin
We sought to evaluate immediate and delayed micro-tensile bond strength of Panavia F2.0 and Multilink Sprint resin cement to superficial, deep and cervical dentin. Thirty-six freshly extracted non-carious human molars were sectioned in the mesiodistal direction to expose three different dentin regions including superficial dentin (1 mm below the dentine-enamel junction), deep dentin (1 mm above...
متن کاملEvaluation of Tensile Bond Strength between Dentin and Metallic Copings Using Different Resin Cements
Statement of the Problem: For a successful clinical outcome, luting agents should have a high bond strength. Bond failure is still one of the main reasons of restoration failures. Purpose: The present study was designed to comparatively evaluate the retention of metallic copings using different resin luting cements. Materials and Method: In the present experimental study, 40 intact premolar tee...
متن کاملEvaluation of the Effect of Sodium Hypochlorite Irrigant on Pull-out Bond Strength of FRC Posts Using Different Resin Cements
Introduction: To evaluate the effects of using sodium hypochlorite irrigant on pull-out bond strength of self-etch and self-adhesive resin cements to dentin. Methods: Sixty intact premolars were decoronated and the root canals were prepared by step-back technique. The teeth were divided into two groups according to the irrigant used during root canal treatment: 5.25% sodium hypochlorite and nor...
متن کاملSodium Hypochlorite Irrigation and Its Effect on Bond Strength to Dentin
Effective shaping and cleaning of root canals are essential for the success of endodontic treatment. Due to the complex anatomy of root canal spaces, the use of various instrumentation techniques alone is not effective in producing bacteria-free root canal spaces. Irrigation, disinfectants, rinses, and intervisit medications are used in conjunction with the mechanical instrumentation to ensure ...
متن کاملمنابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
عنوان ژورنال:
journal of dental materials and techniquesجلد ۵، شماره ۴، صفحات ۱۸۹-۱۹۵
میزبانی شده توسط پلتفرم ابری doprax.com
copyright © 2015-2023