ZrB2-SiC-ZrC coating on ZrC ceramics deposited by plasma spraying
نویسندگان
چکیده
منابع مشابه
سنتز و بررسی خواص نانو پودرکامپوزیتی ZrC-ZrB2-SiC
In this research, ZrC-ZrB2-SiC nanocomposite powder was synthesized by carbothermal and borocarbotermal reduction methods. Zirconium silicate was first milled for four hours Then eight mixtures of raw materials were prepared. Finally, the samples were pyrolyzed at 800 ° C for two hours and then heat-treated at 1500 ° C for 30 minutes under an argon atmosphere. X-ray diffraction (XRD) and scanni...
متن کاملProcessing, Mechanical and Optical Properties of Additive-Free ZrC Ceramics Prepared by Spark Plasma Sintering
In the present study, nearly fully dense monolithic ZrC samples are produced and broadly characterized from microstructural, mechanical and optical points of view. Specifically, 98% dense products are obtained by Spark Plasma Sintering (SPS) after 20 min dwell time at 1850 °C starting from powders preliminarily prepared by Self-propagating High-temperature Synthesis (SHS) followed by 20 min bal...
متن کاملFabrication and inspection of C/Cf-ZrB2-ZrC-SiC and C/Cf-ZrB2-SiC composite parts resistant to ablation by pressureless sintering method
In this research, the aim is to achieve strong and ablation-resistant composite parts C / Cf-ZrB2-ZrC-SiC and C / Cf-ZrB2-SiC by non-pressure sintering method. C / Cf-ZrB2-SiC samples were prepared using synthesized ZrB2 and SiC powders between layers of resin-impregnated carbon fabric. After pressing with pressure 5 times at 1600 وC and heat treatment for 2 hours in a controlled atmosphere fur...
متن کاملC/C-ZrB2-ZrC-SiC Composite Derived from Polymeric Precursor Infiltration and Pyrolysis Part 2: Mechanical and Ablation Properties
Mechanical and ablation properties of the 2D C/C-ZrB2-ZrC-SiC composites with a fiber volume fraction of 17.6%, fabricated by infiltration and co-pyrolysis of blended polymeric precursors, were studied in this Part II. Flexural strength and fracture toughness of the composites were found to be influenced strongly by the thickness of the deposited pyrolytic carbon interphase, a composite with th...
متن کاملThe Effect of the Mg Content on Mechanosynthesis of ZrB2–SiC–ZrC Composite in the Mg/ZrSiO4/B2O3/C System
The influence of magnesium content on the mechanosynthesis of ZrB2–SiC–ZrC composite in Mg/ZrSiO4/B2O3/C mixture was investigated. Thermodynamic evaluations revealed that the amount of Mg played a main role, thereby; the overall reaction enthalpy and adiabatic temperature (Tad) changed by variation of magnesium content. According to differential thermal analysis (DTA) results, after 45min milli...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Results in Physics
سال: 2019
ISSN: 2211-3797
DOI: 10.1016/j.rinp.2019.102550