Workability and Corrosion Resistance of High Purity Chromium.
نویسندگان
چکیده
منابع مشابه
Chromium and insulin resistance.
Insulin resistance leads to the inability of insulin to control the utilization and storage of glucose. It is associated initially with elevated levels of circulating insulin followed by glucose intolerance which may progress to type 2 diabetes, hyperlipidaemia, hypertension, obesity and cardiovascular diseases. While the causes of these diseases are multifactorial, one nutrient that is associa...
متن کاملthe relationship between academic self-concept and academic achievement in english and general subjects of the students of high school
according to research, academic self-concept and academic achievement are mutually interdependent. in the present study, the aim was to determine the relationship between the academic self-concept and the academic achievement of students in english as a foreign language and general subjects. the participants were 320 students studying in 4th grade of high school in three cities of noor, nowshah...
Tarnish Resistance, Corrosion and Stress Corrosion Cracking of Gold Alloys
Tarnishing, corrosion and stress corrosion cracking (SeC) of gold alloys are related phenomena. They present problems when they occur in gold jewellery, dental gold alloys and electronic devices. They are exploited, however, in the depletion gilding and finishing of gold jewellery; and in the extraction, refining and fire assaying of gold. There is still much that is not known about these pheno...
متن کاملTribological Behavior of Reinforced and Unreinforced High Chromium Cast Iron
In this paper, the metal matrix composites containing 22 wt % Cr, 2.5 wt % C and 2 to 16 volume percent TiC were processed by solidifying Fe-Cr-Ti-C in which precipitation of titaniumcarbide and chromium carbide occurred. The microstructure and abrasion resistance of in-situ synthesized composites were compared with the unreinforced high chromium white cast iron (HCWCI) containing 22 w. t. % C...
متن کاملEffect of Chromium on Corrosion Behavior of P110 Steels in CO2-H2S Environment with High Pressure and High Temperature
The novel Cr-containing low alloy steels have exhibited good corrosion resistance in CO₂ environment, mainly owing to the formation of Cr-enriched corrosion film. In order to evaluate whether it is applicable to the CO₂ and H₂S coexistence conditions, the corrosion behavior of low-chromium steels in CO₂-H₂S environment with high pressure and high temperature was investigated using weight loss m...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Materia Japan
سال: 1994
ISSN: 1340-2625,1884-5843
DOI: 10.2320/materia.33.69