Weldability of Al-Si Coated High Strength Martensitic Steel
نویسندگان
چکیده
منابع مشابه
Investigation of Transformation Induced Plasticity in High Al–low Si TRIP Steel
This study was conducted in order to investigate the influence of plastic deformation on the transformation of retained austenite in a TRIP steel with a high content of Al and a low content of Si. To the aim, appropriate treatments were used to produce the starting material (TRIP steel). The microstructure of the obtained steel was composed of bainite and phases including ferrite and retained a...
متن کاملCORROSION BEHAVIOR OF ZINC COATED STEEL REBAR IN HIGH-STRENGTH REINFORCED CONCRETE
A large number of reinforced concrete structures subjected to chloride ions. Two basicapproaches for preventing corrosion of reinforcing steel embedded in concrete are: Increasing theconsolidation of concrete and using different coating on rebars. In present research steel rebarsare coated in different ways: a) 40 µm of zinc electroplated on steel rebar b) Zinc powder withepoxy paste (zinc rich...
متن کاملWeldability Investigation of Fine-grained S1100ql Steel
I. Samardžić, Faculty of Mechanical Engineering Slavonski Brod, Croatia, A. Ćorić, Bratstvo, Novi Travnik, Bosnia and Herzegovina, M. Dunđer, Department for Polytechnic, University of Rijeka, Croatia. This paper presents the results of weldability investigation on welded joints made of fine grained high-strength S1100QL steel. The investigations are performed on two welded plates by HV 10 hardn...
متن کاملMetallurgical investigation in weldability of Aluminium Silicon coated boron steel with different coating thickness
Hot-pressed aluminium and silicon coated boron steel is used in the car industry where high tensile strength is of great importance, such as in the safety cage of a car where deformation has to be kept to a minimum in case of a collision. After hot-pressing the AlSi-boron steel shows excellent properties with high tensile strength, minimal spring back and also shows good protection against corr...
متن کاملHigh-Cycle, Push–Pull Fatigue Fracture Behavior of High-C, Si–Al-Rich Nanostructured Bainite Steel
The high-cycle, push-pull fatigue fracture behavior of high-C, Si-Al-rich nanostructured bainitic steel was studied through the measurement of fatigue limits, a morphology examination and phase composition analysis of the fatigue fracture surface, as well as fractography of the fatigue crack propagation. The results demonstrated that the push-pull fatigue limits at 10⁷ cycles were estimated as ...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Periodica Polytechnica Transportation Engineering
سال: 2013
ISSN: 0303-7800,1587-3811
DOI: 10.3311/pptr.7113