Wearing Resistance of Metal Coating Layers after Laser Beam Heat Treatment
نویسندگان
چکیده
Laser heat treatment (LHT) is applied herein after coating. Evaluation of the results was performed by studying microstructures via metallographic SEM/EDX microscopy, and mechanical properties were analyzed in terms microscopic hardness abrasion resistance. The objective this study to investigate effect LHT on wear resistance metal coatings. indicate influence microstructure chemical composition electrodes microhardness coatings (MCs).
منابع مشابه
Size reduction of a semiconductor nanowire laser using metal coating
We explore the possibility of coating semiconductor nanowires with metal (Ag) to reduce the size of nanowire lasers operating at photon energies around 0.8–2 eV. Our results show that the material gain of a typical III-V semiconductor in nanowire may be sufficient to compensate Joule losses of such metal as Ag. The most promising mode to achieve lasing seem to be TM01 near its cutoff. To calcul...
متن کاملElectronic Supplementary Information Polymer membrane wearing a mineral coating for enhanced curling resistance and surface wettability
Materials Polypropylene microfiltration membranes were obtained from Membrana GmbH (Germany) and Beijing Normal University (China), respectively. One was prepared by thermally induced phase separation with mean pore size of 0.2 μm and porosity of 75%, another was prepared by biaxially orientation with mean pore size of 0.20.02 μm and porosity of 45%. Poly(vinylidene fluoride) (PVDF) microfiltr...
متن کاملEffect of Heat Treatment Time on the Characteristics of Coating Formed on Nanocrystalline Finemet Foils
In the present research, amorphous Fe73.5Si13.5B9Nb3Cu1 Finemet foils, 21-26µm in thickness and 5mm in width, were prepared by Planar Flow Casting (PFC) process. Wound cores of amorphous Finemet foils were simultaneously annealed and heat treated at 540°C for 60, 120 and 240 minutes in steam and air flow to form oxide insulating coating layer on both surfaces of the foils. The structure of nano...
متن کاملExperimental demonstration of laser damage caused by interface coupling effects of substrate surface and coating layers.
The laser damage resistance of the coatings for high-power laser systems depends greatly on the surface quality of the substrate. In our work, experimental approaches were employed to understand the interface coupling effect of the substrate surface and coatings on the laser resistance of the coatings. A 1064 nm anti-reflection (AR) coating was deposited by an e-beam coater onto fused silica wi...
متن کاملTreatment of scars after aesthetic surgery utilizing of a combination of pulsed dye laser and fractional CO2 laser
Background and Aim: Undesirable appearance of the scar tissue after aesthetic surgery can affect the outcomes and patient satisfaction. In recent years, early laser therapy had been encouraged to reduce the scar tissue formation. However, the available evidence regarding the outcomes of laser therapy utilizing combined lasers are limited. In the current study, the effects of combined laser ther...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Coatings
سال: 2023
ISSN: ['2079-6412']
DOI: https://doi.org/10.3390/coatings13091645