Wear Reduction of Wheel Specimens by Duplex Shot Peening in Dry Rolling/Sliding Contact Tests
نویسندگان
چکیده
منابع مشابه
Effects of Plasma ZrN Metallurgy and Shot Peening Duplex Treatment on Fretting Wear and Fretting Fatigue Behavior of Ti6Al4V Alloy
A metallurgical zirconium nitride (ZrN) layer was fabricated using glow metallurgy using nitriding with zirconiuming prior treatment of the Ti6Al4V alloy. The microstructure, composition and microhardness of the corresponding layer were studied. The influence of this treatment on fretting wear (FW) and fretting fatigue (FF) behavior of the Ti6Al4V alloy was studied. The composite layer consiste...
متن کاملMe5656 - Mechanics of Contact & Lubrication Term Project Shot Peening Process
Shot peening is a process where compressive residual stresses are generated at the surface of the processed part by impacting small hard particles to the surface in order to increase the fatigue resistance of the part. In this work, a general literature survey of shot peening process is presented. Survey is mainly focused on mechanics and numerical simulation of the process. Effects of various ...
متن کاملReduction of aircraft tyre wear by pre - rotating wheel using
Heavy aircraft main landing gear tyres skid immediately after touchdown as result of the high slip ratio between the tyres and runway, which lead to tyre wear and smoke. In this paper, the tyre wear is modelled on the Archard theory using ANSYS mechanical transient, to reveal the wheel’s dynamic and the tyre tread wear. The wheel’s dynamic and the amount of wear are calculated for initially sta...
متن کاملSide Effects of Shot Peening on Fatigue Crack Initiation Life
Shot peening beneficial effects on fatigue life of mechanical components are well known. However, there are some reports in the literature that indicate inappropriate shot peening parameters tend to reduce the fatigue life. It is therefore, the purpose of this study to find a logical quantitative justification for these observations. Using finite element method, a dynamic elastic-plastic simula...
متن کاملInvestigation of Wear Mechanism in Quenched and Tempered Medium Carbon-High Chromium Martensitic Steel Using Dry Sand/Rubber Wheel
The aim of the present study was to investigate the effect of quenching and tempering temperatures on the microstructure, mechanical properties and the wear characteristics of medium carbon-high chromium wear resistant steel. In addition, the dominant wear mechanisms were studied. For this purpose, austenitizing and tempering temperatures were selected in the ranges of 900- 1000 °C and 300- 500...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Quarterly Report of RTRI
سال: 2007
ISSN: 0033-9008,1880-1765
DOI: 10.2219/rtriqr.48.225