Wear behavior of Ti1-xAlxN-based coatings during turning

Significant elastic anisotropy in Ti1-xAlxN alloys

Wear behavior of ZrAlN coated cutting tools during turning

In this study we explore the cutting performance of ZrAlN coatings. WC:Co cutting inserts coated by cathodic arc evaporated Zr1-xAlxN coatings with x between 0 and 0.83 were tested in a longitudinal turning operation. The progress of wear was studied by optical microscopy and the used inserts were studied by electron microscopy. The cutting performance was correlated to the coating composition ...

Evaluation of Microstructure and Wear Behavior of Iron-based Hard - facing Coatings on the Mo40 Steel

Mo40 low-alloy steels are mostly used to produce industrial components such as crane wheels which are exposed to abrasive wear. However, during working conditions, their wear resistance is reduced after a while due to its low hardness. With increasing abrasive wear, the dimensions of components decrease and they need to be repaired for surface modification. In this regard, hard overlay coatings...

evaluation of microstructure and wear behavior of iron-based hard - facing coatings on the mo40 steel

mo40 low-alloy steels are mostly used to produce industrial components such as crane wheels whichare exposed to abrasive wear. however, during working conditions, their wear resistance is reduced aftera while due to its low hardness. with increasing abrasive wear, the dimensions of components decreaseand they need to be repaired for surface modification. in this regard, hard overlay coatings ar...

Linköping University Post Print Pressure enhancement of the isostructural cubic decomposition in Ti1−xAlxN