Wear Behavior and Microstructure of Thermally Sprayed NiCrBSiFeC and Composite NiCrBSiFeC-WC(Co) Coatings
نویسندگان
چکیده
In this work, a study was carried out on the friction and wear behavior of flame thermal sprayed NiCrBSiFeC-WC(Co) composite NiCrBSiFeC coatings subjected to severe conditions. For purpose, remelted samples were tested in reciprocating conditions based cylinder-on-flat configuration. The assessment achieved using scanning electron microscopy (SEM) 3D optical profilometry. microstructure mechanical properties investigated SEM, EDS XRD techniques as along with indentation tests. tribological substrate successfully studied thanks tests conducted an adapted multi test apparatus. results show that both induced significant increase steel hardness resistance due formation precipitates high well dispersed within ultra-crystalline structure. Besides, adding WC(Co) leads coating further improved. return, it increases coefficient (COF) coatings’ roughness. Furthermore, improvements surface hardness, roughness coating-substrate adhesion attained after remelting process for coatings. Wear tracks investigations indicated dry sliding configuration promote several mechanisms may occur simultaneously.
منابع مشابه
Effect of Carbide Particle Size on the Microstructure, Mechanical properties, and Wear Behavior of HVOF-sprayed WC-17% Co Coatings
This study investigates the effect of carbide particle size on the microstructure, mechanical properties, and abrasive wear resistance of WC-17%Co HVOF-sprayed coatings. The characteristics of WC-1, WC-2, and WC-3 coatings with carbide sizes of 1 µm, 0.9 µm, and 0.5 µm, respectively, were also investigated. WC-1 coating experienced the maximum carbon loss of 42%, while WC-2 and WC-3 coatings un...
متن کاملThe Study of High Temperature Oxidation behavior of Different Microstructures of HVOF Thermally Sprayed Coatings
Improvement of thermally sprayed coating properties by microstructure modification has been considered as a significant solution. Therefore, in this research the effect of dissolved oxygen content and post heat treatment on the formation and distribution of secondary phase particles, particularly in nano-scale in the coatings during spraying and after that were studied. Ni-5 wt% Al powders were...
متن کاملEvaluation of Microstructure and Wear Behavior of Iron-based Hard - facing Coatings on the Mo40 Steel
Mo40 low-alloy steels are mostly used to produce industrial components such as crane wheels which are exposed to abrasive wear. However, during working conditions, their wear resistance is reduced after a while due to its low hardness. With increasing abrasive wear, the dimensions of components decrease and they need to be repaired for surface modification. In this regard, hard overlay coatings...
متن کاملEffect of WC Concentration on Abrasive Wear Properties of the Thermally Sprayed WC -Ni Coatings
In this work the effects of WC concentration on abrasive wear behavior by thermally sprayed WC coating was evaluated using three body abrasive wear tester. A different combination of WC and NI coatings were deposited on steel substrates by flame spraying using powder with different WC concentrations (0 %, 12.5 %, 25 %, and 50 %). Flame torch was used for heating and coating of process. Microstr...
متن کاملMicrostructure and Properties of Plasma Sprayed Nanostructural ZrO2 Coatings
Plasma sprayed zirconia deposits have been employed in wide applications for thermal protection. Recently, the use of nanostructural surface represents an alternative for improving the performance of these coatings. The present paper reviewed the works in this field at our research group, including synthesis of nanostructural ZrO2 powders, influence of spraying parameters on microstructure and ...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Materials Science
سال: 2021
ISSN: ['1068-820X', '1573-885X']
DOI: https://doi.org/10.5755/j02.ms.24478