Wear and corrosion of niobium carbide coated AISI 52100 bearing steel
نویسندگان
چکیده
منابع مشابه
Check Tic-coated Tungsten Carbide Tool Wear in Machining Steel
In industrial production systems, including the most important factors in the economic field machining operations, reduce tool wear due to abrasive nature of the phenomenon on many factors, including temperature Lathe tool, influences, machining conditions (cutting speed, speed losses, forcing to rebuild parts of the manufacturing tolerances disassemble tool wear is caused by the phenomenon, as...
متن کاملKinetic Study of Niobium Carbide Coating Formation on AISI L2 Steel using Thermo-Reactive Deposition Technique
In the present study, Thermo-Reactive Deposition method (TRD) in a molten bath was used to form niobium carbide coating on AISI L2 steel. The coating was formed in five different composition of borax (Na2B4O7), boric acid (B2O3), and ferro-niobium. For all of the five compositions of molten bath, niobium carbide coating treatment was carried out at 1173 K, 1273 K, and 1373 K for 2, 4 and 8 hour...
متن کاملOptimization of Surface Roughness in Hard Turning of AISI 4340 Steel using Coated Carbide Inserts
The use of multilayer coated carbide tool in hard turning has several advantages over grinding process such as; reduction of processing costs, increased productivity, short cycle time, compatible surface roughness and less enviornment problems without the use of cutting fluid. In the present study, an attempt has been made to evaluate the performance of multilayer coated carbide inserts during ...
متن کاملSTUDY ON NIOBIUM CARBIDE COATING FORMATION ON AISI L2 STEEL USING THERMO-REACTIVE DEPOSITION METHOD
In the present research, to form niobium carbide coating on the surface of AISI L2 steel Thermo-Reactive Deposition method (TRD) in a molten bath was used. Niobium carbide coating treatment was carried out at 1173 K, 1273 K, and 1373 K for 2, 4, and 8 hours. The molten bath contained 20wt.% borax (Na2B4O7), 5 wt.% boric acid (B2O3), and 75 wt.% ferro-niobium. The presence and properties of...
متن کاملCorrosion Behaviour of Nickel Coated AISI 316 Stainless Steel as a Function of Annealing Temperature
AISI 316 stainless steels were coated with 250 nm Ni film by electron beam deposition and post-annealed at different temperatures with a nitrogen flow of 600 cm3min-1 nitrogen. The prepared samples were corrosion tested in 1.0 M sulphuric acid solution using potentiodynamic technique. Crystallographic and morphological structure of the samples were analyzedanalysed by X-ray diffraction (XRD) an...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Surface and Coatings Technology
سال: 2015
ISSN: 0257-8972
DOI: 10.1016/j.surfcoat.2015.08.036