Vickers Indentation Cracking of Ion-Exchanged Glasses: Quasi-Static vs. Dynamic Contact
The indentation deformation and cracking responses of ion-exchanged glasses were measured using quasi-static and dynamic loading cycles. Two glass types were compared, a normal glass that deforms to a large extent by a shearing mechanism and a damage-resistant glass that comparatively deforms with less shear and more densification. The quasi-static indentation cracking threshold for median/radi...
متن کاملContact Behaviour of Composite Laminate under Quasi-Static Indentation Load
A viable solution to the ever-demanding weight-saving target in aerospace industry is the replacement of conventional engineering alloys with composite materials in primary structures. A major concern to the effective use of composite laminates is the substantial reduction in the compressive strength when the contact force has exceeded the delamination threshold load (DTL). This paper focuses o...
متن کاملOn the deformation morphology of bulk metallic glasses underneath a Vickers indentation
The techniques commonly used for observing the deformation mechanisms underneath a Vickers indentation in metallic glasses (chemical etching, bonded interface) induce artefacts such as cracks or semi-circular shear-bands. We propose an alternative technique based on the propagation of indentation corner cracks through a pre-existing imprint, which is possible in metallic glasses such as iron-ba...
متن کاملXAFS Studies of Silver Environments in Ion-Exchanged Glasses
The X-ray absorption fine structure (XAFS) technique was used to analyze the structural geometry of Ag atoms introduced into soda-lime silicate glass and soda aluminosilicate glass by ion-exchange methods. The results show that Ag ions in aluminosilicate glass are coordinated by about two oxygens and the nearest-neighbor Ag-O distance increases when the Ag-for-Na ion-exchange ratio is larger th...
متن کاملInteraction between Deformation and Crack Initiation under Vickers Indentation in Na2O–TiO2–SiO2 Glasses
An observed minimum in the critical crack initiation load at Poisson’s ratio (ν) of 0.21–0.22 in Na2O–TiO2–SiO2 glasses was investigated. Vickers indentation was used to examine hardness and average cracking length, fracture toughness was measured through the single-edge pre-cracked beam method, and volumes of densification and shear flow around indents were measured using atomic force microsco...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Frontiers in Materials
سال: 2017
ISSN: 2296-8016
DOI: 10.3389/fmats.2017.00004