Very High Cycle Fatigue Properties of Carburized Steel by Ultrasonic Torsional Fatigue Testing
نویسندگان
چکیده
منابع مشابه
High Cycle Fatigue Property of Carburized 20Cr Gear Steel under Axial Loading
Abstract: The high cycle fatigue property of carburized 20Cr gear steel was experimentally investigated under axial loading with a stress ratio of zero. The test results show that this steel exhibits gradually decreasing S-N characteristics, and the fatigue strength corresponding to 109 cycles is about 455 MPa. Based on the observation of fracture surfaces, the interior inclusion fisheye-induce...
متن کاملRedesigning axial-axial (biaxial) cruciform specimens for very high cycle fatigue ultrasonic testing machines
The necessity to increase performances in terms of lifetime and security in mechanical components or structures is the motivation for intense research in fatigue. Applications range from aeronautics to medical devices. With the development of new materials, there is no longer a fatigue limit in the classical sense, where it was accepted that the fatigue limit is the stress level such that there...
متن کاملEffect of Low Cycle Fatigue Predamage on Very High Cycle Fatigue Behavior of TC21 Titanium Alloy
The effect of low cycle fatigue (LCF) predamage on the subsequent very high cycle fatigue (VHCF) behavior is investigated in TC21 titanium alloy. LCF predamage is applied under 1.8% strain amplitude up to various fractions of the expected life and subsequent VHCF properties are determined using ultrasonic fatigue tests. Results show that 5% of predamage insignificantly affects the VHCF limit du...
متن کاملInfluence of Operating Conditions on High-cycle Fatigue Properties of High Alloyed Steel X20
In this paper, the effect of service temperature and life on high-cycle fatigue properties of base metal, steel X20 CrMoV 12-1, has been analysed. The effect of service conditions has been analysed by testing the new material and material that was in service for 116000 hours. The investigations have included determination of permanent fatigue strength at room and operating temperature. These in...
متن کاملDigital Micromirror Device (DMD)-Based High-Cycle Torsional Fatigue Testing Micromachine for 1D Nanomaterials
Fatigue behavior of nanomaterials could ultimately limit their applications in variable nano-devices and flexible nanoelectronics. However, very few existing nanoscale mechanical testing instruments were designed for dedicated fatigue experiments, especially for the challenging torsional cyclic loading. In this work, a novel high-cycle torsion straining micromachine, based on the digital microm...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of the Society of Materials Science, Japan
سال: 2010
ISSN: 1880-7488,0514-5163
DOI: 10.2472/jsms.59.938