Variable Amplitude Loading Test of Transverse Stiffener Joints for Fatigue Design of Steel Highway Bridges.
نویسندگان
چکیده
منابع مشابه
Lifetime prediction of adhesive joints subjected to variable amplitude fatigue
Almost all structural applications of adhesive joints will experience cyclic loading and in most cases this will irregular in nature, a form of loading commonly known as variable amplitude fatigue (VAF). This paper is concerned with the VAF of adhesively bonded joints and has two main parts. In the first part, results from the experimental testing of adhesively bonded single lap joints subjecte...
متن کاملStrip yield modelling of fatigue crack under variable amplitude loading
The results from ‘strip yield’ approach of the FASTRAN type models of plasticity induced crack closure effects of fatigue cracks subjected to variable amplitude loadings are presented. The strip yield results are compared with authors’ finite element (FE) and experimental results. It has been observed that the strip yield model is seen to be fundamentally limited by choice of α (constraint fact...
متن کاملStochastic fatigue damage modeling under variable amplitude loading
A general methodology for stochastic fatigue life prediction under variable amplitude loading is proposed in this paper. The methodology combines a nonlinear fatigue damage accumulation rule and a stochastic S–N curve representation technique to achieve this objective. The nonlinear damage accumulation rule proposed in this paper improves the deficiencies inherent in the linear damage accumulat...
متن کاملfinite element based fatigue assessment of corrugated steel web beams in highway bridges
this paper presents a finite element analysis and its related experimental test of corrugated steel web beams subjected to fatigue loading. a particular focus in this study was set on the fatigue failure arising from the web-to-flange welded joint of the corrugated steel web beam. a detailed three-dimensional finite element model which explicitly includes the geometry of the web-to-flange welds...
متن کاملAnalyses of Fatigue and Fatigue-crack Growth under Constant- and Variable-amplitude Loading
Studies on the growth of small cracks have led to the observation that fatigue life of many engineering materials is primarily “crack growth” from micro-structural features, such as inclusion particles, voids, slip-bands or from manufacturing defects. This paper reviews the capabilities of a plasticity-induced crack-closure model to predict fatigue lives of metallic materials using “small-crack...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of the Society of Materials Science, Japan
سال: 1995
ISSN: 1880-7488,0514-5163
DOI: 10.2472/jsms.44.557