Upconversion luminescence of Er<sup>3+</sup>/Yb<sup>3+</sup> Co-Doped Sb<sub>2</sub>O<sub>3</sub>-WO<sub>3</sub>-Li<sub>2</sub>O Antimonate Glasses
نویسندگان
چکیده
منابع مشابه
Enhancing luminescence in lanthanide-doped upconversion nanoparticles.
The enthusiasm for research on lanthanide-doped upconversion nanoparticles is driven by both a fundamental interest in the optical properties of lanthanides embedded in different host lattices and their promise for broad applications ranging from biological imaging to photodynamic therapy. Despite the considerable progress made in the past decade, the field of upconversion nanoparticles has bee...
متن کاملSecond harmonic generation and two-photon luminescence upconversion in glasses doped with ZnSe nanocrystalline quantum dots
We report two-photon excited emission in borosilicate glasses doped with ZnSe nanocrystalline quantum dots. The emission, predominantly near the two-photon energy and detected in the direction of the excitation beam, is in the visible, and the fundamental excitation is the near-infrared output of a tunable femtosecond laser. Depending on the two-photon energy, timeand frequency-resolved measure...
متن کاملLaser-diode-excited intense luminescence and green-upconversion in erbium-doped bismuth-germanate-lead glasses.
We investigate the spectroscopic properties of the 1.5-microm emission from the (4)I(13/2)-->(4)I(15/2) transition of Er(3+) ions in bismuth-germanate-lead glasses for applications in broadband fiber amplifiers. The emission peak locates at 1532nm with a full width at half-maximum (FWHM) of approximately 65nm. The measured lifetime and the calculated emission cross-section of this transition ar...
متن کاملSpectroscopic properties and upconversion mechanisms in Er3+-doped fluoroindate glasses.
Fluorindate glasses containing 1,2,3,4 ErF3 mol % were prepared in a dry box under argon atmosphere. Absorption, Stokes luminescence ~under visible and infrared excitation!, the dependence of S3/2, I11/2, and I13/2 lifetimes with Er concentration, and upconversion under Ti-saphire laser excitation at l5790 nm were measured, mostly at T577 and 300 K. The upconversion results in a strong green em...
متن کاملLuminescence Properties of TeO2-LiF-Gd2O3 Glasses
In this work, the structural properties and spectroscopic behavior 80 mol.%TeO2-20mol.%LiF glasses which were doped with 0. 05, 0. 2 mole% Gd2O3 have been studied. It was shown that, by increasing the amount of Gd2O3 the glass stability was decreased. The PL emissions at 431nm and 627nm wavelengths were distinguished by 320nm excitation. The FT-IR analysis showed deformed TeO4 groups in these ...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: New Journal of Glass and Ceramics
سال: 2011
ISSN: 2161-7554,2161-7562
DOI: 10.4236/njgc.2011.12006