Unfolding the early fatigue damage process for CFRP cross-ply laminates
نویسندگان
چکیده
منابع مشابه
Failure Criterion for Two-Ply Plain-Weave CFRP Laminates
We present an experimentally-based failure criterion for symmetric two-ply plain-weave laminates of carbon-fiber reinforced plastic. The criterion is formulated in terms of six force and moment stress resultants and consists of a set of three inequalities, related to in-plane, bending, and combined in-plane and bending types of failure. All failure parameters in the criterion are measured direc...
متن کاملUltrasonic NDE Techniques for Impact Damage Inspection on CFRP Laminates
This study investigates the different types of ultrasonic inspection, when applied to assess the impact damage in Carbon Fiber Reinforced Plastic CFRP laminates. The study surveys the two most used ultrasonic testing approaches first; namely the pulse-echo and the through-transmission modes. Then, the manuscript discusses and analyzes the enhanced ultrasonic testing methods that use the polar s...
متن کاملImpact Damage Detection of Toughened CFRP Laminates with Time Domain
Laminated Carbon Fiber Reinforced Polymer (CFRP) composites are very effective in weight saving in aeronautical structural components. For these laminated CFRP structures, it is, however, difficult to detect damage such as delamination, matrix cracks, and local fiber breakages caused by low velocity impact loading In the previous study in 2009, Time Domain Reflectometry (TDR) method was applied...
متن کاملDamage in Textile Laminates of Various Inter-ply Shift
Deformation mechanisms and failure of textile laminates are strongly affected by inter-layer configurations – a mutual shift of the plies. To model it within a traditional framework, one must construct a representative volume element (RVE), which includes all the plies. This is a time consuming and computationally expensive work. As an alternative, the paper suggests boundary conditions (BC) im...
متن کاملPost-cure shape errors of ultra-thin symmetric CFRP laminates: Effect of ply-level imperfections
This paper discusses the effect of misalignments in ply orientation, uniform variations in ply thickness, and through-thickness thermal gradients on the post-cure shape errors for symmetric cross-ply laminates constructed from ultra-thin composite materials. Photogrammetry-based surface measurements are performed for laminates cured at elevated temperatures. Significant out-of-plane shape error...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: International Journal of Fatigue
سال: 2020
ISSN: 0142-1123
DOI: 10.1016/j.ijfatigue.2020.105820