Unexpected Precipitation of a Re-Rich Phase in Single Crystal Superalloy CMSX-4 during Thermal Exposure
نویسندگان
چکیده
منابع مشابه
In- and Out-of Phase Thermomechanical Fatigue of a Ni-Based Single-Crystal Superalloy
In this study, the difference between in-phase (IP) and out-of-phase (OP) thermomechanical fatigue (TMF) cycling from 100 to 750 ◦C has been investigated for the Ni-based single-crystal superalloy MD2. In addition, two different crystal orientations were studied, the 〈001〉 and 〈011〉 orientations respectively. When comparing IP and OP TMF lives, a strain range dependency is found for the 〈001〉 d...
متن کاملEffect of Thermal History on Microstructural Changes in Aluminized Nickel-Based Single-Crystal Superalloy
The effect of the thermal history on microstructural changes in aluminized and Pt-aluminized Ni-based single-crystal superalloys was investigated. The superalloy substrates were first electropolished to get rid of the residual surface strain. Then, Pt was electrodeposited and vacuum annealing was conducted for some of the substrates, and aluminized and Pt-aluminized specimens were prepared usin...
متن کاملFatigue crack initiation in a notched single-crystal superalloy component
In this paper, the fatigue crack initiation in notched single-crystal test specimens of material MD2 is investigated and analysed. A critical plane approach is adopted, in which the total strain ranges on the discrete slip planes are evaluated. Furthermore, a Coffin-Manson type of expression is used to describe the number of cycles to fatigue crack initiation. This relation is determined from a...
متن کاملCarbides Evolution in a Ni-16Mo-7Cr Base Superalloy during Long-Term Thermal Exposure
The effect of long-term thermal exposure on the carbide evolution in a Ni-16Mo-7Cr base superalloy was investigated. The results show that M12C carbides are mainly precipitated on the grain boundaries during thermal exposure, and the primary massive M₆C carbides can be completely transformed to M12C carbides in situ at temperatures above 750 °C for long-term thermal exposure. The transformation...
متن کاملJoint Development of a Fourth Generation Single Crystal Superalloy
A new, fourth generation, single crystal superalloy has been jointly developed by GE Aircraft Engines, Pratt & Whitney and NASA. The focus of the effort was to develop a turbine airfoil alloy with long-term durability for use in the High Speed Civil Transport. In order to achieve adequate long-time strength improvements at moderate temperatures and retain good microstructural stability, it was ...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of Metallurgy
سال: 2012
ISSN: 1687-9465,1687-9473
DOI: 10.1155/2012/308568