Tungsten oxide nanowires grown on amorphous-like tungsten films
نویسندگان
چکیده
منابع مشابه
Tungsten oxide nanowires grown on carbon cloth as a flexible cold cathode.
Figure 1 . a) Optical images of the carbon cloth with TONWs, left-inset and right-inset show the optical images of a carbon cloth with TONWs under slight bending and severe bending, respectively. b,c) SEM images of the carbon cloth before and after growing TONWs, respectively. Inset [∗] X. H. Zhang , Y. Z. Cao , X. Xiao , W. M. Sun , Prof. Y. H. Gao , Prof. J. Zhou , Prof. Z. L. Wang Wuhan Nati...
متن کاملCarbide formation in tungsten-containing amorphous carbon films by annealing
Tungsten-containing amorphous carbon films were produced by dual magnetron sputter deposition. The formation of carbide phases after heat treatment in inert gas at temperatures up to 2800 K was investigated by X-ray diffraction for tungsten concentrations below 25 at%. After deposition, each film consists of an amorphous carbon matrix with atomically dispersed W inclusions. Annealing up to 2800...
متن کاملOptical constants of amorphous, transparent titanium-doped tungsten oxide thin films.
We report on the optical constants and their dispersion profiles determined from spectroscopic ellipsometry (SE) analysis of the 20%-titanium (Ti) doped of tungsten oxide (WO3) thin films grown by sputter-deposition. The Ti-doped WO3 films grown in a wide range of temperatures (25-500 °C) are amorphous and optically transparent. SE data indicates that there is no significant interdiffusion at t...
متن کاملPolaron and Phonon Properties in Proton Intercalated Amorphous Tungsten Oxide Thin Films
We report on the evolution of the polaron and phonon mode properties in amorphous tungsten oxide thin films measured by spectroscopic ellipsometry in the infrared to ultraviolet spectral regions as a function of the intercalated proton density. A parametric physical model dielectric function is presented, which excellently describes the ellipsometry data over a large intercalated charge-density...
متن کاملSelective formation of tungsten nanowires
We report on a process for fabricating self-aligned tungsten (W) nanowires with polycrystalline silicon core. Tungsten nanowires as thin as 10 nm were formed by utilizing polysilicon sidewall transfer technology followed by selective deposition of tungsten by chemical vapor deposition (CVD) using WF6 as the precursor. With selective CVD, the process is self-limiting whereby the tungsten formati...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Nanotechnology
سال: 2015
ISSN: 0957-4484,1361-6528
DOI: 10.1088/0957-4484/26/36/365601