Transverse Cracking in CFRP Laminates with Interlaminar-Resin Layers.

Impact Damage Detection of Toughened CFRP Laminates with Time Domain

Laminated Carbon Fiber Reinforced Polymer (CFRP) composites are very effective in weight saving in aeronautical structural components. For these laminated CFRP structures, it is, however, difficult to detect damage such as delamination, matrix cracks, and local fiber breakages caused by low velocity impact loading In the previous study in 2009, Time Domain Reflectometry (TDR) method was applied...

Electromagnetic Shielding Property of Cfrp Composite Laminates

Cracking in brittle laminates from concentrated loads

A study is made of the crack resistance of multilaminates consisting of brittle layers interleaved with compliant interlayers and bonded to compliant substrates. Specific attention is paid to flexure-generated radial cracks in the undersurfaces of individual glass layers from concentrated loads applied at the top surfaces. A proposed condition for acceptance of such multilayer systems is that r...

Ultrasonic NDE Techniques for Impact Damage Inspection on CFRP Laminates

This study investigates the different types of ultrasonic inspection, when applied to assess the impact damage in Carbon Fiber Reinforced Plastic CFRP laminates. The study surveys the two most used ultrasonic testing approaches first; namely the pulse-echo and the through-transmission modes. Then, the manuscript discusses and analyzes the enhanced ultrasonic testing methods that use the polar s...

Strength and Modulus Degradation of CFRP Laminates from Fiber Misalignment

Fiber reinforced polymer (FRP) laminates are being used as external reinforcement for strengthening concrete members. The performance of unidirectional FRP laminates is highly dependent on fiber orientation with respect to applied load direction. In the case of fabrication by manual lay-up, it is possible to have fiber plies installed with improper orientation. In this project, the degradation ...