Transparent Sol-Gel Oxyfluoride Glass-Ceramics with High Crystalline Fraction and Study of RE Incorporation
نویسندگان
چکیده
منابع مشابه
Upconversion luminescence in Er-doped germanate-oxyfluoride and tellurium-germanate-oxyfluoride transparent glass-ceramics
Upconversion luminescence has been studied for Er in a germanate-oxyfluoride and a tellurium-germanate-oxyfluoride transparent glass-ceramic using 800 nm excitation. Significantly increased upconversion luminescence was observed from transparent glass-ceramics compared with that from their corresponding as-prepared glasses. In addition to a strong green emission centered at 545 nm from S3/2 sta...
متن کاملTransparent Glass-Ceramics Produced by Sol-Gel: A Suitable Alternative for Photonic Materials
Transparent glass-ceramics have shown interesting optical properties for several photonic applications. In particular, compositions based on oxide glass matrices with fluoride crystals embedded inside, known as oxyfluoride glass-ceramics, have gained increasing interest in the last few decades. Melt-quenching is still the most used method to prepare these materials but sol-gel has been indicate...
متن کاملTransparent Oxyfluoride Nano-Glass Ceramics Doped with Pr3+ and Pr3+–Yb3+ for NIR Emission
1 Instituto de Cerámica y Vidrio, Consejo Superior de Investigaciones Científicas (CSIC), Madrid, Spain, 2 Microdevices for Photonics Laboratory (MIP-LAB), Istituto di Fisica Applicata “Nello Carrara”, Consiglio Nazionale delle Ricerche (CNR), Sesto Fiorentino, Italy, 3 Museo Storico della Fisica e Centro Studi e Ricerche Enrico Fermi, Roma, Italy, 4 Instituto de Catálisis y Petroleoquímica, Co...
متن کاملUpconversion properties of a transparent Er3þ–Yb3þ co-doped LaF3–SiO2 glass-ceramics prepared by sol–gel method
Transparent 0.1ErF3–0.1YbF3–5LaF3–94.8SiO2 (mol%) glass-ceramics was prepared by sol–gel method. Efficient upconversion emissions at 379, 407, 450, 490, 520, 540 and 660 nm were observed under 973 nm excitation. The signal at 379 nm is only 4.5 times weaker than the signal at 520 nm, that is readily visible by the naked eyes even with a pump power of 27 mW, indicating that this sample is a very...
متن کاملDistribution of Nd3+ ions in oxyfluoride glass ceramics
It has been an open question whether Nd3+ ions are incorporated into the crystalline phase in oxyfluoride glass ceramics or not. Moreover, relative research has indicated that spectra characters display minor differences between before and after heat treatment in oxyfluoride glass compared to similar Er3+-, Yb3+-, Tm3+-, Eu3+-, etc.-doped materials. Here, we have studied the distribution of Nd3...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Nanomaterials
سال: 2019
ISSN: 2079-4991
DOI: 10.3390/nano9040530