Transitional Wear of Plasma Spray Cr2O3 and Cr3C2 Coatings Deposited on Low Carbon Steel
نویسندگان
چکیده
In the present work, transitional wear of atmospheric plasma sprayed Cr2O3 and Cr3C2 coatings on low carbon steel substrate have been investigated with coating thickness 100μm 200μm. The produced coated uncoated mild samples were characterized by means microscopic examinations, hardness sliding tests for varying parameters load, speed, distance, SEM analysis carried out characterization studies worn surface samples. obtained results revealed that rate was much lower in followed substrate. When comparison to chromium oxide composite carbide showed better improved
منابع مشابه
Phlogopite glass-ceramic coatings on stainless steel substrate by plasma spray
Macor coatings on 316 alloys substrates were prepared by plasma spraying. The crystallization temperature, thermal expansion coefficient of mica glass-ceramic were at 900ºC and 40× 10−7/◦C respectively. The microhardness of obtained glass-ceramic coating was 6.8GPa and the coefficient friction was 0.98 .
متن کاملDetermination of Optical Properties in Germanium Carbon Coatings Deposited by Plasma Enhanced Chemical Vapor Deposition
In this research, Germanium-carbon coatings were deposited on ZnS substrates by plasma enhanced chemical vapor deposition (PECVD) using GeH4 and CH4 precursors. Optical parameters of the Ge1-xCx coating such as refractive index, Absorption coefficient, extinction coefficient and band gap were measured by the Swanepoel method based on the transmittance spectrum. The results showed that the refra...
متن کاملCorrosion of Cold Spray Deposited Copper Coating on Steel Substrates
The corrosion behavior of copper cold spray coatings on a carbon steel substrate was compared to that of commercially available wrought copper under the conditions anticipated in a nuclear waste repository. Corrosion potential and linear polarization resistance measurements were conducted over 90 d to 120 d in 3.0 mol/L NaCl under anoxic (1) and oxygenated-toanoxic (2) conditions to simulate th...
متن کاملEvaluation of Microstructure and Wear Behavior of Iron-based Hard - facing Coatings on the Mo40 Steel
Mo40 low-alloy steels are mostly used to produce industrial components such as crane wheels which are exposed to abrasive wear. However, during working conditions, their wear resistance is reduced after a while due to its low hardness. With increasing abrasive wear, the dimensions of components decrease and they need to be repaired for surface modification. In this regard, hard overlay coatings...
متن کاملPhosphor-Doped Thermal Barrier Coatings Deposited by Air Plasma Spray for In-Depth Temperature Sensing
Yttria-stabilized zirconia (YSZ)-based thermal barrier coating (TBC) has been integrated with thermographic phosphors through air plasma spray (APS) for in-depth; non-contact temperature sensing. This coating consisted of a thin layer of Dy-doped YSZ (about 40 µm) on the bottom and a regular YSZ layer with a thickness up to 300 µm on top. A measurement system has been established; which include...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: International journal of emerging science and engineering
سال: 2022
ISSN: ['2319-6378']
DOI: https://doi.org/10.35940/ijese.d2524.0310422