Transition of Fracture Mechanism of Ductile Cast Iron in Extremely Low Cycle Fatigue.
نویسندگان
چکیده
منابع مشابه
Effect of Dynamic Strain Aging on Isothermal (473K) Low Cycle Fatigue of Ferritic Ductile Cast Iron
The ferritic ductile iron (FCD400) is widely used as industrial material. As regards to its high temperature application, fatigue at elevated temperature, and advanced mechanical properties has been investigated and clarified. In low cycle fatigue (LCF), the S-N curve is presented by the relation of plastic strain to the number of cycles as fatigue life, which can be predicted by the Manson-Cof...
متن کاملLinkage between Ductile Fracture and Extremely Low Cycle Fatigue of Inconel 718 under Multiaxial Loading Conditions
Ductile fracture and extremely low cycle fatigue (ELCF) [1] are two common failure modes in aircraft engines and turbomachinery designs [2]; however, the linkage between these two failure modes under multi-axial loading conditions has never been systematically studied. Inconel 718 (IN718) is one type of high temperature alloys widely used in turbomachines. Specially designed specimens and tests...
متن کاملFatigue Performance of Forged Steel and Ductile Cast Iron Crankshafts
Fatigue is the primary cause of failure of crankshafts in internal combustion engines. The cyclic loading conditions and the stress concentrations in the crank pin fillets are unavoidable, and can result in fatigue failure. The objectives of this study were to compare the fatigue behavior of forged steel and ductile iron crankshafts from a one-cylinder engine as well as to determine if the fati...
متن کاملUltra-Low Cycle Fatigue Fracture Life of a Type of Buckling Restrained Brace
Buckling restrained braced frames (BRBFs) for seismic load resistance have been widely used in recent years. One of the key requirements for a buckling restrained brace is to sustain large plastic deformations under severe ground motions. The core of a buckling restrained brace is prone to fatigue fracture under cyclic loading. The earthquake induced fracture type of the core plate in a bucklin...
متن کاملEffects of Silicon on Mechanical Properties and Fracture Toughness of Heavy-Section Ductile Cast Iron
The effects of silicon (Si) on the mechanical properties and fracture toughness of heavy-section ductile cast iron were investigated to develop material for spent-nuclear-fuel containers. Two castings with different Si contents of 1.78 wt.% and 2.74 wt.% were prepared. Four positions in the castings from the edge to the center, with different solidification cooling rates, were chosen for micros...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: TRANSACTIONS OF THE JAPAN SOCIETY OF MECHANICAL ENGINEERS Series A
سال: 1993
ISSN: 0387-5008,1884-8338
DOI: 10.1299/kikaia.59.291