Transient Liquid Phase Bonding of Ni-base Single Crystal Superalloy, CMSX-2.
نویسندگان
چکیده
منابع مشابه
Fretting on the cubic face of a single-crystal Ni-base superalloy at room temperature
Fretting experiments were conducted on the (10 0) crystal (cubic) face of a single crystal Ni-base superalloy in two directions, /10 0S and /110S, to study the effect of crystallographic orientation on the fretting response in both partial slip and gross slip regimes. The study involved point contacts using a tungsten carbide (WC) ball with radius 10 mm tested at room temperature. Ball indentat...
متن کاملIn- and Out-of Phase Thermomechanical Fatigue of a Ni-Based Single-Crystal Superalloy
In this study, the difference between in-phase (IP) and out-of-phase (OP) thermomechanical fatigue (TMF) cycling from 100 to 750 ◦C has been investigated for the Ni-based single-crystal superalloy MD2. In addition, two different crystal orientations were studied, the 〈001〉 and 〈011〉 orientations respectively. When comparing IP and OP TMF lives, a strain range dependency is found for the 〈001〉 d...
متن کاملTransient liquid phase bonding of AISI 304L stainless steels with the austenitic and martensitic microstructures
In the present study, the effect of time and base metal microstructure on the Transient Liquid Phase (TLP) bonding of 304L stainless steel was studied. TLP was performed at 1050 0C for 5 and 60 minutes on the coarse grain austenitic and martensitic microstructure using BNi-2 interlayer. To prepare martensitic microstructure, as-received 304L was rolled at -15 0C up to 80% rolling reduction. TEM...
متن کاملTransient liquid phase bonding of AISI 304L stainless steels with the austenitic and martensitic microstructures
In the present study, the effect of time and base metal microstructure on the Transient Liquid Phase (TLP) bonding of 304L stainless steel was studied. TLP was performed at 1050 0C for 5 and 60 minutes on the coarse grain austenitic and martensitic microstructure using BNi-2 interlayer. To prepare martensitic microstructure, as-received 304L was rolled at -15 0C up to 80% rolling reduction. TEM...
متن کاملEvaluating the Effect of Ta/W Ratio on Microstructure and Stress Rupture Properties of Ni-Based Single Crystal Superalloy PWA1483
In this study, the effect of Ta/W ratio on the microstructure and stress rupture properties of Ni-based single crystal (SX) superalloy PWA1483 was investigated. For this purpose, single crystal (SX) superalloys with different Ta/W ratios (0.75, 1.0, 1.32 and 1.5 in wt.%) were fabricated. The alloys were directionally solidified by Bridgman method under the same solidification condition at withd...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: ISIJ International
سال: 1995
ISSN: 0915-1559
DOI: 10.2355/isijinternational.35.1298