Transformation Superplasticity in Pure-Iron under Rapid Heating
نویسندگان
چکیده
منابع مشابه
Enhanced superplasticity in commercially pure titanium alloy
The superplasticity of commercially pure titanium alloy at high temperature was studied and the dynamic recrystallization phenomenon of the alloy was investigated by using electron back scattered diffraction. A two-step deformation method was used to increase the ductility of the alloy from 188% to 243%. 2004 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.
متن کاملHydrogen-induced transformation superplasticity in zirconium
Commercially-pure zirconium is alloyed and dealloyed repeatedly with hydrogen at 810 C, thereby cyclically triggering phase transformations between hydrogen-free a-Zr and hydrogen-alloyed b-Zr. Under an externally applied tensile stress, the internal mismatch stresses produced by the a-b transformations are biased, resulting in the accumulation of strain increments after each chemical cycle in ...
متن کاملTRANSFORMATION SUPERPLASTICITY OF SUPER a2 TITANIUM ALUMINIDE
ÐTransformation superplasticity of an intermetallic Ti3Al-based alloy (Super a2) is demonstrated by thermal cycling about the a2/b transformation temperature range under a uniaxial tensile biasing stress. Failure strains up to 610% were recorded at a stress of 3 MPa, compared with 110% for deformation by isothermal creep at the same stress. The strain increment produced during each half-cycle i...
متن کاملTransformation-mismatch Superplasticity in Reinforced and Unreinforced Titanium
Samples of commercial-purity titanium, with and without 10 vol.% TiC particulates. were thermally cycled about the allotropic transformation temperature of titanium. Thermal ratcheting was small for both unstressed materials. Upon application of an external uniaxial tensile stress, unreinforced titanium exhibited large strain increments, resulting from the biasing by the applied stress of the v...
متن کاملTensile fracture during transformation superplasticity of Ti–6Al–4V
During thermal cycling through the a–b phase transformation under the action of a small external biasing stress, Ti alloys exhibit an average deformation stress exponent of unity and achieve superplastic strains. We report tensile experiments on Ti–6Al–4V with an applied stress of 4.5 MPa, aimed at understanding the failure processes during transformation superplasticity. The development of cav...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of the Japan Institute of Metals and Materials
سال: 1974
ISSN: 0021-4876,1880-6880
DOI: 10.2320/jinstmet1952.38.8_725