Titanium Aluminide-Based Composite Deposits with Dispersed Nitride Particles Produced by Reactive Thermal Spraying
نویسندگان
چکیده
منابع مشابه
Thermal stability of a-titanium in contact with titanium nitride
The thermal stability of an a-Ti film in contact with a d-TiN film in the structure of a TiN/Ti/TiN film stack on SiO2 substrates was studied by in situ sheet resistance (Rs) measurement, Auger electron spectroscopy, glancing angle x-ray diffractometry, cross-sectional transmission electron microscopy, scanning electron microscopy, and atomic force microscopy. It was found that nitrogen dissolv...
متن کاملDecorative Titanium Nitride Colored Coatings on Bell-Metal by Reactive Cylindrical Magnetron Sputtering
The transition metal nitrides like titanium nitride exhibit very interesting color variation properties depending on the different plasma deposition conditions using cylindrical magnetron sputtering method. It is found in this deposition study that nitrogen partial pressure in the reactive gas discharge environment plays a significant role on the color variation of the film coatings on bell-met...
متن کاملFatigue behavior and damage modeling of SCS-6/titanium/titanium aluminide hybrid laminated composite
The fatigue behavior of the unnotched and notched silicon carbide fiber-reinforced titanium/titanium aluminide hybrid laminated composite was investigated at room temperature. The evolution of microstructural damage and its effect on stiffness and strength degradation was quantified as a function of loading cycles and applied stress levels. Fatigue crack propagation behavior and damage mechanis...
متن کاملFormation and Properties of Ni-Based Amorphous Metallic Coating Produced by HVAF Thermal Spraying
A highly dense Ni59Zr20Ti16Si2Sn3 partial amorphous metallic coating, about 500mm thick, was fabricated by means of HVAF (High Velocity Air Fuel) thermal spraying. Amorphous alloy powders produced by using gas atomization were used for HVAF thermal spraying to produce an amorphous metallic coating. Microstructural investigation showed that crystallization and oxidation occurred during thermal s...
متن کاملThe Effects of Beryllium Additions on the Oxidation of Nickel Aluminide and Titanium Aluminide Based Intermetallics
The effects of Be additions on the oxidation behavior of ~-NiAl in moist air at 1000°C and borderline alumina-forming y (TiAI) + Laves Ti-Al-Cr based alloys at 800°C and 1000°C in dry and moist air were investigated. The addition of Be to ~-NiAl suppressed the formation of transient alumina, and resulted in the formation of a protective BeAl20 4 spinel phase. In dry air, the addition of Be to t...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of the Japan Institute of Metals and Materials
سال: 2002
ISSN: 0021-4876,1880-6880
DOI: 10.2320/jinstmet1952.66.7_784