Threshold Stress for High-Temperature Deformation of Dispersion-Strengthened Alloys.
نویسندگان
چکیده
منابع مشابه
Model for creep threshold stress in precipitation-strengthened alloys with coherent particles
The general climb model for creep threshold stress for dislocations interacting with incoherent particles is modified for the case of coherent precipitates, by taking into account elastic interactions between matrix dislocations and particles due to particle/matrix stiffness and lattice mismatches. The model is in qualitative agreement with experimental data for the Al–Sc system. 2002 Acta Mate...
متن کاملHigh Temperature Deformation Mechanism in Hierarchical and Single Precipitate Strengthened Ferritic Alloys by In Situ Neutron Diffraction Studies
The ferritic Fe-Cr-Ni-Al-Ti alloys strengthened by hierarchical-Ni2TiAl/NiAl or single-Ni2TiAl precipitates have been developed and received great attentions due to their superior creep resistance, as compared to conventional ferritic steels. Although the significant improvement of the creep resistance is achieved in the hierarchical-precipitate-strengthened ferritic alloy, the in-depth underst...
متن کاملMicrostructure, Mechanical and Tribological Properties of Oxide Dispersion Strengthened High-Entropy Alloys
A novel metal matrix composite CrMnFeCoNi with Y₂O₃ as reinforcement phase was designed and manufactured by mechanical alloying and spark plasma sintering. After sintering at 900 °C for 5 min, the microstructure consisted of a FCC matrix and Y₂O₃ nanoparticles. The addition of 0.25 wt % Y₂O₃ increased the room temperature tensile strength of the CrMnFeCoNi base from 868 MPa to 1001 MPa, while t...
متن کاملComparison of Ductile-to-Brittle Transition Behavior in Two Similar Ferritic Oxide Dispersion Strengthened Alloys
The ductile-to-brittle transition (DBT) behavior of two similar Fe-Cr-Al oxide dispersion strengthened (ODS) stainless steels was analyzed following the Cottrell-Petch model. Both alloys were manufactured by mechanical alloying (MA) but by different forming routes. One was manufactured as hot rolled tube, and the other in the form of hot extruded bar. The two hot forming routes considered do no...
متن کاملHigh Temperature Deformation of Twin-Roll Cast Al-Mn-Based Alloys after Equal Channel Angular Pressing
Twin roll cast Al-Mn- and Al-Mn-Zr-based alloys were subjected to four passes of equal channel angular pressing. The resulting grain size of 400 nm contributes to a significant strengthening at room temperature. This microstructure is not fully stable at elevated temperatures and recrystallization and vast grain growth occur at temperatures between 350 and 450 °C. The onset of these microstruct...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Proceedings of the Japan Academy, Series B
سال: 1993
ISSN: 0386-2208,1349-2896
DOI: 10.2183/pjab.69.167