Three-point bending strength and cyclic bending fatigue strength of hot-pressed silicon nitride containing a small crack.
نویسندگان
چکیده
منابع مشابه
Strength of small-diameter round and tapered bending members
An early focus on structural use of processed rather than round timber resulted in an underestimation of the structural advantages of retaining the natural form of small-diameter round timber. In the round and tapered form, timbers are not susceptible to the strength-reducing effects of diving grain and exposed juvenile wood. Fiber continuity around knots on the surface of a debarked log rarely...
متن کاملFatigue strength of bovine articular cartilage-on-bone under three-point bending: the effect of loading frequency
BACKGROUND The objective of this study was to determine the influence of loading frequency on the failure of articular cartilage-on-bone specimens under three-point bending. METHODS In this study, cyclic three-point bending was used to introduce failure into cartilage-on-bone specimens at varying loading frequencies. Sinusiodally varying maximum compressive loads in the range 40-130 N were ap...
متن کاملExploration of the Customized Fixtures for the Evaluation of Three-point Bending Strength of Dental Resin Composites
Introduction: This study aimed to devise customized fixtures for the evaluation of three-point bending strength (TPBS) of resin-based dental composites (RBCs). Materials and Methods: A cube-shaped jig made out of wood with dimensions of 105×105×101 mm was prepared in this study. A 20-mm-diameter hole was made in the center of the wooden jig. In addition, a stai...
متن کاملBending strength of delaminated aerospace composites.
Buckling-driven delamination is considered among the most critical failure modes in composite laminates. This paper examines the propagation of delaminations in a beam under pure bending. A pre-developed analytical model to predict the critical buckling moment of a thin sub-laminate is extended to account for propagation prediction, using mixed-mode fracture analysis. Fractography analysis is p...
متن کاملModeling the strain-rate dependence of fatigue life of hot- pressed silicon nitride
This paper presents the results of a micromechanical model used to explain the strain-rate dependence of the compression fatigue lives of amorphous and crystalline grain boundary phase; denoted by ABP and CBP silicon nitrides, respectively. When the strain-rate is changed from 400 to 0.01/s, the fatigue lives of both materials, evaluated at a peak stress of 3.2 GPa, increased by more than two o...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: TRANSACTIONS OF THE JAPAN SOCIETY OF MECHANICAL ENGINEERS Series A
سال: 1990
ISSN: 0387-5008,1884-8338
DOI: 10.1299/kikaia.56.1771