Three-Point Bending Fatigue Test of TiAl6V4 Titanium Alloy at Room Temperature
نویسندگان
چکیده
منابع مشابه
Corrosion Fatigue Studies on a Bulk Glassy Zr-Based Alloy under Three-Point Bending
Corrosion fatigue (CF) tests were carried out on bulk glassy Zr52.5Cu17.9Al10Ni14.6Ti5 (Vitreloy 105) samples under load-controlled three-point bending conditions with a load ratio of R = 0.1 in 0.01 M Na2SO4 + 0.01 M NaCl electrolyte. During cyclic testing, the bar-shaped specimens were polarized in situ at constant potentials and the current was monitored. Three different anodic potentials wi...
متن کاملImprinting bulk amorphous alloy at room temperature
We present investigations on the plastic deformation behavior of a brittle bulk amorphous alloy by simple uniaxial compressive loading at room temperature. A patterning is possible by cold-plastic forming of the typically brittle Hf-based bulk amorphous alloy through controlling homogenous flow without the need for thermal energy or shaping at elevated temperatures. The experimental evidence su...
متن کاملIdentification of Low Cycle Fatigue Parameters of High Strength Low-alloy (hsla) Steel at Room Temperature
S. Bulatović, Yugoslav River Shipping, Serbia, Lj. Milović, University of Belgrade, Faculty of Technology and Metallurgy, Serbia, A. Sedmak, University of Belgrade, Faculty of Mechanical Engineering, Serbia, I. Samardžić, University of Osijek, Mechanical Engineering Faculty, Slavonski Brod, Croatia Low cycle fatigue test was performed in ambient atmosphere at room temperature. Cycle loading of ...
متن کاملRoom temperature fracture processes of a near-a titanium alloy following elevated temperature exposure
Near-a titanium alloys are used at higher temperatures than any other class of titanium alloys. As a consequence of thermal exposure, these components may develop locally elevated oxygen concentrations at the exposed surface which can negatively impact ductility and resistance to fatigue crack initiation. In this work, monotonic and fatigue fracture mechanisms of Ti–6Al–2Sn– 4Zr–2Mo–0.1Si sampl...
متن کاملHeusler alloy showing room temperature half - metallicity at the surface
In this article we investigate the surface spin polarization in a 100 nm Co 2 Cr 0.6 Fe 0.4 Al (CCFA) film grown ex situ epitaxially on MgO(100) with a 10 nm Fe buffer layer by means of spin resolved photoemission. We show that a careful in situ preparation of the sample surface leads to values for the room temperature spin polarization up to 45% at the Fermi level. To our knowledge, this is th...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Advances in Materials Science and Engineering
سال: 2019
ISSN: 1687-8434,1687-8442
DOI: 10.1155/2019/2842416