Three-dimensional fractographic analysis of total fracture areas in 6082 aluminium alloy specimens under fatigue bending with controlled damage degree
نویسندگان
چکیده
منابع مشابه
Corrosion Fatigue Studies on a Bulk Glassy Zr-Based Alloy under Three-Point Bending
Corrosion fatigue (CF) tests were carried out on bulk glassy Zr52.5Cu17.9Al10Ni14.6Ti5 (Vitreloy 105) samples under load-controlled three-point bending conditions with a load ratio of R = 0.1 in 0.01 M Na2SO4 + 0.01 M NaCl electrolyte. During cyclic testing, the bar-shaped specimens were polarized in situ at constant potentials and the current was monitored. Three different anodic potentials wi...
متن کاملThree-dimensional fracture analysis of CT specimens with a ductile damage model based on endochronic plasticity theory
For many fracture problems of practical engineering importance, the three-dimensional effects are significant and a three-dimensional analysis for the problems is thus required. In this paper, an endochronic theory coupled with anisotropic damage is first established, which is actually an elasto-plastic damage theory coupled with isotropic-nonlinear kinematic hardening. The ductile damage evolu...
متن کاملFatigue and Anisotropic behaviours of cold rolled AA1200 Aluminium Alloy
This study examines the fatigue and anisotropy behaviour of cold rolled AA1200 aluminium alloy for light weight automotive connecting rod application. Aluminium (Al) 1200 ingots were melted at temperature of 680 0C (after one hour of heating) cast in sand mould and cast samples homogenized for 6 hrs at 480 0C. The cold rolling process was carried out after homogenisation for 10, 20, 30, 40 and ...
متن کاملThree-Dimensional Geostatistical Analysis of Rock Fracture Roughness and Its Degradation with Shearing
Three-dimensional surface geometry of rock discontinuities and its evolution with shearing are of great importance in understanding the deformability and hydro-mechanical behavior of rock masses. In the present research, surfaces of three natural rock fractures were digitized and studied before and after the direct shear test. The variography analysis of the surfaces indicated a strong non-line...
متن کاملEffects of temperature gradient magnitude on bending angle in laser forming process of aluminium alloy sheets
Laser forming is a thermal forming process which uses laser beam irradiation to produce the desired final forms. In this article, the effect of temperature gradient across Al 6061-T6 aluminum sheets on bending angle is studied. Input parameters including laser power, scan velocity, beam diameter, and sheet thickness are the effective process parameters which influence the temperature gradient....
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Mechanics of Materials
سال: 2020
ISSN: 0167-6636
DOI: 10.1016/j.mechmat.2020.103410