Three-dimensional crack observation, quantification and simulation in a quasi-brittle material
نویسندگان
چکیده
منابع مشابه
Direct observation and image-based simulation of three-dimensional tortuous crack evolution inside opaque materials.
We present a combined novel methodology to study the three-dimensional complex geometry of a tortuous crack and identify the essential features of the crack and its propagation inside a heterogeneous material. We find that some severe damage events occur unexpectedly below a local mode-I crack within the sample; we realize that the severe plastic zone of the local mode-I crack is shifted down b...
متن کاملRandom Lattice-Particle Simulation of Statistical Size Effect in Quasi-Brittle Structures Failing at Crack Initiation
The modeling of statistical size effect of concrete structures that fail at crack initiation is studied, with special attention to the interaction between the autocorrelation length and the size of the failure zone. The mechanical failure of concrete is modeled by a network of axial springs with degrading stiffness. The heterogeneity of concrete is idealized by spatial variation of the tensile ...
متن کاملFrom rate-dependent to quasi-static brittle crack propagation
On the base of many experimental results, e.g. [18], [19], [21], [12], the object of our analysis is a rate-dependent model for the propagation of a crack in brittle materials. Our goal is a mathematical study of the evolution equation in the geometries of the ’Single Edge Notch Tension’ (SENT) and of the ’Compact Tension’ (ASTM-CT). Besides existence and uniqueness, emphasis is placed on the r...
متن کاملThree-dimensional Simulation of Fretting Crack Nucleation and Growth
Fretting nucleation models and three-dimensional finite element analyses are used to compute the fretting fatigue life for metallic components. The models predict crack nucleation cycles and location(s). Discrete crack growth simulations provide stress intensity factor histories, with multiple, non-planar, three-dimensional cracks possible. The histories are input into crack growth rate model(s...
متن کاملTowards the treatment of boundary conditions for global crack path tracking in three-dimensional brittle fracture
The aim of the present paper is a systematic elab1 oration of a three dimensional finite element analysis tool for 2 discontinuous fracture in brittle solids. Brittle or quasi-brittle 3 fracture usually occurs when a material reaches the limit of its 4 strength and no plastic deformation has been observed prior 5 to failure. In the present approach, this kind of failure is char6 acterized by th...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Acta Materialia
سال: 2013
ISSN: 1359-6454
DOI: 10.1016/j.actamat.2013.07.011