Thixoforging of Low Carbon Steel SAE1006 Backward Thixoextrusion
نویسندگان
چکیده
منابع مشابه
Failure Investigation of Hydrogen Blistering on Low-strength Carbon Steel
The current study assesses the root causes of hydrogen blisters on low strength carbon steel equipment. For this purpose, some experiments including hardness test, non-destructive test (NDT), metallography, and fractograpghy are conducted. The microstructure of two blisters is assessed by means of optical microscopy and scanning electron microscopy (SEM). The microstructural studies show that t...
متن کاملStatic Strain Aging Behavior of Low Carbon Steel Drawn Wire
The static strain aging is a phenomenon that can change the mechanical properties of low carbon steels. Thus, the static strain aging behavior of low carbon steel wires after drawing process is studied. To do so, the wires are austenitized at different temperatures and cooled in different rates. Then the wires are drawn and aged at a specific temperature and time. Before and after aging of each...
متن کاملRecrystallization Behavior of Deep Drawing Low Carbon Steel Sheets Produced by Mobarakeh Steel Plant
In the present work the recrystallization behavior of deep drawing grade Al-killed low carbon steel sheets produced by Mobarakeh Steel Plant (MSP) has been studied. Salt bath isothermal annealing has b...
متن کاملElectrochemical Behaviour of Low Carbon Steel in Aqueous Solutions
An effective way of assessing corrosion in pipelines before serious consequences occur is to use tools that can predict the future of a pipeline through an understanding of its present state and the mechanisms of corrosion. In this work electrochemical methods such as liner and tafel polarization resistance were used to evaluate corrosion. Most metal corrosion occurs via electrochemical reactio...
متن کاملOptimization of the parameters of low-carbon steel (EN10130) welding using friction stir welding method
Friction-stir welding process is a novel method of solid state welding, which produces heat due to friction between the pin, the shoulder and the workpiece. This heat causes a paste area. Shoulder pressure and pin spin cause edges integration and lead to welding. In this study, firstly, the feasibility of welding of steel sheet (EN10130) with a thickness of 1.5mm has been tested by 58 experim...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Procedia Engineering
سال: 2017
ISSN: 1877-7058
DOI: 10.1016/j.proeng.2017.10.972