Thermal stress of plate and pipe occurred during dipping in the molten zinc bath. Liquid metal embrittlement of welded joint of steel during hot dip galvanizing. Report 2.
نویسندگان
چکیده
منابع مشابه
the effect of e-64 on the developmental competence of sheep cocs during in vitro maturation
in the present study, the effect of e-64 at different concentrations (0.5, 1, 5 and 10 µm) added to (1) the ivm medium on oocyte nuclear maturation and developmental competence of ovine oocytes, and (2) to the ivc medium on embryonic development of ovine embryos were investigated.
effectiveness of hedstroum files and rotary k3 instruments in removal of obturation materials during retreatment in curved canals
چکیده ندارد.
15 صفحه اولREACTION KINETICS OF THE FORMATION OF INTERMETALLIC Fe – Zn DURING HOT - DIP GALVANIZING OF STEEL
P. Pokorny, J. Kolisko, L. Balik – Czech Technical University – Klokner Institute, Prague, Czech Republic P. Novak – Institute of Chemical Technology, Prague, Czech Republic This review article mainly describes the composition of intermetallic Fe Zn, i.e. zeta (ζ), delta (δ1k + δ1p), gamma1 (Γ1) and gamma (Γ) on galvanized steel during low temperature galvanization (t ~ 450 °C). It gives detail...
متن کاملLiquid Metal Corrosion of 316L Stainless Steel, 410 Stainless Steel, and 1015 Carbon Steel in a Molten Zinc Bath
Corrosion tests of 1015 low-carbon steel and two stainless steels (410 and 316L) were conducted in a pure zinc bath (99.98 wt pct Zn) in order to better understand the reaction mechanisms that occur during the degradation of submerged hardware at industrial general (batch) galvanizing operations. Through this testing, it was found that, in general, 316L stainless steel showed the best dissoluti...
متن کاملsimulation and experimental studies for prediction mineral scale formation in oil field during mixing of injection and formation water
abstract: mineral scaling in oil and gas production equipment is one of the most important problem that occurs while water injection and it has been recognized to be a major operational problem. the incompatibility between injected and formation waters may result in inorganic scale precipitation in the equipment and reservoir and then reduction of oil production rate and water injection rate. ...
ذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: QUARTERLY JOURNAL OF THE JAPAN WELDING SOCIETY
سال: 1985
ISSN: 0288-4771
DOI: 10.2207/qjjws.3.347