Thermal Shock Fracture Behavior of Alumina Ceramics Containing Pores.
نویسندگان
چکیده
منابع مشابه
Fracture toughness and thermal shock of tool and turbine ceramics
The behaviour of some commercial tool carbides and turbine ceramics has been investigated in regard to resistance to crack initiation, crack propagation and retained strength after thermal shock. New data are provided, particularly measurements of the fracture toughness of these materials at actual operating temperatures (up to 1200 ~ C). Many of the materials did not follow the generally accep...
متن کاملTHERMAL FRACTURE OF CERAMICS WITH TEMPERATURE-DEPENDENT PROPERnES
Some aspects of thetmal fracture mechanics of ceramics with temperature-dependent properties are studied. It is first shown that the square-root singular field still prevaiLY in the crack tip region. However, the size of the K-dominant zone may be influenced by the effect of temperature-dependent properties. Then the steady thetmal stress intensity factor in an edge-cracked strip is calculated....
متن کاملThermal-stress resistance and fracture toughness of two tool ceramics
The thermal-stress resistance and fracture strength behaviour of two oxide ceramics (a hot-pressed pure AI203 and a composite ceramic NTK-HC2) subjected to severe thermal shocks have been investigated. The damage resistance parameter (Kic/of)2 for both ceramics is also determined for a wide range of temperatures (25 ~ to 800 ~ C) and cross-head rates (10 -2 cm min -1 ~ 2.5 m sec -1 ). Fracture ...
متن کاملAddition of Alumina to Nanoporous Calcium Titanium Phosphate Glass-Ceramics and its Effects on Crystallization Behavior
Microporous Calcium Titanium Phosphate glass-ceramics have many uses in high-tech industries. For example, they have applications in catalysts industry. In this study, different molar percentages of alumina were added to a glass with P2O5 30, CaO 45, TiO2 25 (mol%) composition. The samples were melted at 1350°C and crystallization heat treatment was performed on...
متن کاملThermal Stress Resistance to Fracture and its Relation to with Resistance to Thermal Fatigue and Shock
Dense Silicon nitride was investigated to determine the effect of its microstructural parameters and densification on thermo-mechanical properties and thermal stress resistance to fracture initiation during a hot or cold mechanical and thermal shock testing. The different materials and microstructures were obtained by changing the parameters such as the type of the powder, additive, forming p...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of the Ceramic Society of Japan
سال: 2002
ISSN: 0914-5400,1882-1022
DOI: 10.2109/jcersj.110.937