Thermal response of DP600 dual-phase steel under ultrasonic fatigue loading
نویسندگان
چکیده
منابع مشابه
Influence of Sudden Column Loss on Dynamic Response of Steel Moment Frames under Blast Loading
Modeling buildings response to blast and subsequent progressive collapse interested more and more researchers during the past two decades. Due to the threat from extreme loading, efforts have been made to develop methods of structural analysis and design. In this paper, progressive collapse capacity of steel moment frames was first investigated using alternate load path method, then a nonlinear...
متن کاملHigh Cycle Fatigue Property of Carburized 20Cr Gear Steel under Axial Loading
Abstract: The high cycle fatigue property of carburized 20Cr gear steel was experimentally investigated under axial loading with a stress ratio of zero. The test results show that this steel exhibits gradually decreasing S-N characteristics, and the fatigue strength corresponding to 109 cycles is about 455 MPa. Based on the observation of fracture surfaces, the interior inclusion fisheye-induce...
متن کاملFatigue strength evaluation of self-piercing riveted cold rolled steel joints under mixed mode loading conditions
Fatigue strength of cross-shaped specimens of SPR joints made of SPCC was evaluated at load angles of 0°, 45°, and 90°. For the static strength at load angles of 0°, 45°, and 90°, the maximum loads were determined to be 4890N, 1969N, and 1611N, respectively. Regarding for the relationship between the load amplitude and the number of cycles (Nf), the results were 014 . 0 3 . 2209 − = f amp N P ,...
متن کاملUltra low cycle fatigue of welded steel joints under multiaxial loading
Ultra low cycle fatigue (ULCF) is a phenomenon that can be summarily defined as the deterioration of material properties under high amplitude cyclic loading, under which failure is reached typically within ten to twenty cycles. This phenomenon is observed in extreme loading scenarios such as earthquakes or exceptional winds where large cyclic strains are expected. Particularly sensitive are str...
متن کاملInterior Fracture Mechanism Analysis and Fatigue Life Prediction of Surface-Hardened Gear Steel under Axial Loading
The interior defect-induced fracture of surface-hardened metallic materials in the long life region has become a key issue on engineering design. In the present study, the axial loading test with fully reversed condition was performed to examine the fatigue property of a surface-carburized low alloy gear steel in the long life region. Results show that this steel represents the duplex S-N (stre...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Materials Science and Engineering: A
سال: 2016
ISSN: 0921-5093
DOI: 10.1016/j.msea.2016.09.025