Thermal cycle control at surface plasma treatment of high carbon steel
نویسندگان
چکیده
منابع مشابه
Duplex Surface Treatment of AISI 1045 Steel via Plasma Nitriding of Titanized Layer
In this Study, surface of medium carbon steel (AISI 1045) was modified by titanizing followed by plasma nitriding. Titanizing was performed using pack cementation method, in a pack mixture of ferrotitanium, ammonium chloride and alumina, at 1223 K for 45 and 180 min. Plasma-nitriding was conducted at two temperatures of 803 and 823 K for 5 h, in a gas mixture of 75%N2+25%H2. The samples were c...
متن کاملInfluence of Thermal Cycle on Temperature Dependent Process Parameters Involved in GTA Welded High Carbon Steel Joints
In this research article a comprehensive investigation has been carried out to determine the effect of thermal cycle on temperature dependent process parameters developed during gas tungsten arc (GTA) welding of high carbon (AISI 1090) steel butt joints. An experiment based thermal analysis has been performed to obtain the thermal history. We have focused on different thermophysical properties ...
متن کاملThe Reactive Chemisorption of Carbon Dioxide at Mg(100) Surface
X-ray photoelectron and electron energy loss spectroscopic (XPS-EELS) studies reveal that the following species are present when a mixture of CO2 and water vapour is exposed to the clean Mg(100) surface at 110K: CO3(a), C(a) CH(a), OH(a). The reactive chemisorptions of CO2 and H2O vapour coadsorbed on a Mg surface ...
متن کاملLife cycle assessment of steel production from iron scrap: a case study at a steel plant
Background and Objective: The steel industry is the world's largest consumer of energy. A large amount of iron waste is produced annually, which its use in the steel industry can be economic. The purpose of this study was to investigate the environmental impacts of the steelmaking from iron scrap as a raw material using a life cycle assessment (LCA) method. Materials and Methods: Simapro softw...
متن کاملGas Solubility of Carbon Dioxide in Poly(lactic acid) at High Pressures: Thermal Treatment Effect
The sorption of carbon dioxide in glassy Poly(lactic acid) (PLA) films was studied by quartz crystal microbalance (QCM) at high pressures. Two thermal treatments, melted and quenched, were performed in PLA with two different L:D contents, 80:20 and 98:2, films and compared with a third thermal protocol, annealed, and used in a previous work. The results obtained show that for pressures higher t...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Ferrous Metallurgy. Bulletin of Scientific , Technical and Economic Information
سال: 2018
ISSN: 2619-0753,0135-5910
DOI: 10.32339/0135-5910-2018-12-81-88