The Yield Condition of Nodular Cast Iron Subjected to Triaxial Stresses

Residual Stresses and Fatigue of Shot Peened Cast Iron

iii

Failure Analysis of a Four Cylinder Diesel Engine Crankshaft Made From Nodular Cast Iron

The premature breakage in some four cylinder diesel engine crankshafts was reported. All crankshafts were failed from the same region. Failures had occurred in the first crankpin, the nearest crankpin to the flywheel. Dynamic analysis and finite element modelling were carried out to determine the state of stress in the crankshaft. FEM results revealed that the first crankpin fillet is the most ...

Modeling of Ultrasonic Testing for Inspection of Nodular Cast Iron Insert

Nodular cast iron insert will be used as the inner component of nuclear fuel disposal canister. The outer cover of the canister is copper tube of 50 mm nominal thickness. Nodular cast iron insert is cast around several steel channels, which also strengthen the structure. The mechanical properties of the cast iron insert will be tested according EN-1563 /1/. According the specifications 100% NDT...

Fatigue Behaviour of Synthetic Nodular Cast Irons

A. Vaško, L. Trško, R. Konečná, Faculty of Mechanical Engineering, University of Žilina, Žilina, Slovak Republic The paper shows the influence of charge composition on microstructure, fatigue properties and failure micromechanisms of nodular cast irons. The additive of metallurgical silicon carbide (SiC) in analysed specimens increases the content of ferrite in the matrix, decreases the size of...

The Microsegregation Pattern of Aluminum and Silicon in the Matrix Microstructure of the Nodular Cast Irons