The T6 Heat Treatment of Semi-Solid Metal Processed Alloy A356

A solution treatment of 1 hour at 540 o C provided the best results for rheocast alloy A356-T6. Natural aging has a significant influence on the subsequent artificial aging response of the alloy. Arrhenius-type equations were derived to predict the time-to-peak hardness as a function of artificial aging temperature.

متن کامل

Investigation of the T4 and T6 Heat Treatment Cycles of Semi-Solid Processed Aluminium Alloy A356

The heat treatment cycles that are currently applied to semi-solid processed components are mostly those that are in use for dendritic casting alloys. These heat treatments are not necessarily the optimum treatments. It is shown that a decrease of the solution treatment time at 540 o C from 6 hours to 1 hour does not alter the T4 or T6 tensile properties of the SSM processed A356 alloy. Slightl...

متن کامل

Impact Properties of A356-T6 Alloys

The Charpy impact energy of A356 alloys has been measured. Instrumented Charpy impact tests have been conducted at 25, 100, 150, and 200 ~ The Charpy specimens were machined from plate castings or tapered cylindrical castings. The plates were produced in sand molds, and tapered cylinders were produced in water-cooled copper molds. Both unmodified and strontium-modified castings were tested. The...

متن کامل

EFFECT OF T6 HEAT TREATMENT ON MECHANICAL PROPERTIES OF CERAMIC REINFORCED CASTED ALUMINUM ALLOY

Aluminium base alloy (Al-Cu-Si) was reinforced with silicon carbide (SiC) particles, in various percentage compositions from 0-20 wt%. Silicon carbide particle size of 20µm was selected. The molten slurry of SiC reinforced base aluminium metal was casted through green and dry sand casting methods and solidification process was carried out under ambient conditions. A selected population...

متن کامل

EVALUATION OF PRESSURE EFFECT ON HEAT TRANSFER COEFFICIENT AT THE METAL- MOLD INTERFACE FOR CASTING OF A356 AL ALLOY

Abstract: During solidification and casting in metallic molds, the heat flow is controlled by the thermal resistance at the casting-mold interface. Thus heat transfer coefficient at the metal- mold interface has a predominant effect on the rate of heat transfer. In some processes such as low pressure and die-casting, the effect of pressure on molten metal will affect the rate of heat transfer a...

متن کامل

ذخیره در منابع من


  با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید

ژورنال

عنوان ژورنال: The Open Materials Science Journal

سال: 2008

ISSN: 1874-088X

DOI: 10.2174/1874088x00802010006