The stress-magnetic properties of amorphous magnetic alloy.
نویسندگان
چکیده
منابع مشابه
Microstructure and magnetic properties of amorphous Fe51Co12Si16B8Mo5P8 alloy
Fe-based metallic glasses such as FINEMET, NANOPERM and HITPERM usually produced from amorphous precursors in various forms have been intensively studied over the past thirty years, because these materials exhibit a unique combination of soft magnetic properties [1], which is very interesting from a scientifi c point of view. The application of these materials at elevated temperatures is determ...
متن کاملMagnetic Properties of Ni0.3Fe0.7 Alloy Nanowires
The effect of length variation on the magnetic properties of NiFe alloy nanowires electrodeposited into the alumina template was investigated. The diameter (45±2.5 nm) and length (~ 1.9, 7.12, 8.3, 9.5 and 13.3 µm) of the nanowires were estimated from scanning electron microscopy images. Energy dispersive spectroscopy results showed Ni3Fe7 composition of the alloy nanowire...
متن کاملmagnetic properties of ni0.3fe0.7 alloy nanowires
the effect of length variation on the magnetic properties of nife alloy nanowires electrodeposited into the alumina template was investigated. the diameter (45±2.5 nm) and length (~ 1.9, 7.12, 8.3, 9.5 and 13.3 µm) of the nanowires were estimated from scanning electron microscopy images. energy dispersive spectroscopy results showed ni3fe7 composition of the alloy nanowires. the magnetic prope...
متن کاملMagnetic properties of amorphous Ni60Ag40 films
Amorphous Ni–Ag films were obtained on liquid nitrogen cooled Si substrates using DC magnetron sputtering. A series of magnetic and magneto-transport property measurements confirm that the film with Ni to Ag atomic ratio of 60:40 is an alloy of the two elements immiscible in equilibrium, with atomic-level intermixing. The magnetic properties of the new alloy are discussed in comparison with tho...
متن کاملEffect of Cu Addition on Soft Magnetic Properties of Fe–Zr–Si Amorphous Alloy
The effect of Cu addition on the soft magnetic properties of FeZrSi amorphous alloy was investigated by X-ray analysis, TEM observation, and B-H curve tracer. As a melt-spun amorphous ribbon sample was annealed above the crystallization onset temperature, very fine ¡-Fe particles smaller than 315 nm were precipitated and uniformly distributed in an amorphous matrix. Cu addition to FeZrSi am...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of the Magnetics Society of Japan
سال: 1989
ISSN: 0285-0192
DOI: 10.3379/jmsjmag.13.427