The Stress Corrosion Cracking of Copper Alloys (IV)

Tarnish Resistance, Corrosion and Stress Corrosion Cracking of Gold Alloys

Tarnishing, corrosion and stress corrosion cracking (SeC) of gold alloys are related phenomena. They present problems when they occur in gold jewellery, dental gold alloys and electronic devices. They are exploited, however, in the depletion gilding and finishing of gold jewellery; and in the extraction, refining and fire assaying of gold. There is still much that is not known about these pheno...

Stress Corrosion Cracking

The Possible Role of Hydrogen in Stress Corrosion Cracking of Titanium Alloys

The various mechanisms that have been put forward to explain stress-corrosion cracking are briefly summarized. The experimental observations of stress-corrosion cracking in titanium alloys in widely different environmer a are discussed. Evidence from the literature for and against the possibility that hydrogen plays a role in the stress-corrosion cracking of titanium alloys is documented. An ex...

Corrosion Product Film-Induced Stress Facilitates Stress Corrosion Cracking

Finite element analyses were conducted to clarify the role of corrosion product films (CPFs) in stress corrosion cracking (SCC). Flat and U-shaped edge-notched specimens were investigated in terms of the CPF-induced stress in the metallic substrate and the stress in the CPF. For a U-shaped edge-notched specimen, the stress field in front of the notch tip is affected by the Young's modulus of th...

Study of Copper Bearing Alloys Corrosion Characteristics

This paper addresses investigation of the corrosion behavior of copper bearing anodes with high nickel content. Anodes are produced from different solid wastes formed during the copper or nickel row materials treatment. Nickel content in anode samples had values up to 10 mas %. The content of tin, lead and antimony was up to 1 % for each of elements. Sulphuric acid solution, concentration of 17...