The mechanism of emulsion polymerization. II. Branching in polymers prepared by emulsion polymerization techniques
نویسندگان
چکیده
منابع مشابه
Role of Surfactants in Emulsion Polymerization Polymers by design
The determination of an emulsifier’s adsorption properties under conditions similar to those occurring during emulsion polymerization can provide important information to aid in the selection of the most appropriate surfactant for a given system. Results show that the latex particle size is dependent on the strength of emulsifier adsorption (∆Eads) at the particle/aqueous phase interface and is...
متن کاملTowards a consistent mechanism of emulsion polymerization—new experimental details
The application of atypical experimental methods such as conductivity measurements, optical microscopy, and nonstirred polymerizations to investigations of the 'classical' batch ab initio emulsion polymerization of styrene revealed astonishing facts. The most important result is the discovery of spontaneous emulsification leading to monomer droplets even in the quiescent styrene in water system...
متن کاملPolyaniline Nanoparticles Prepared by Micro-Emulsion Polymerization for Corrosion Inhibition of Carbon Steel in 1M HCl
Polyaniline nanoparticles were prepared using oxidation polymerization in micro-emulsion system. Sodium dodecyl sulphate was used as a surfactant which dissolved in hydrochloric acid giving the micellar solution. Potassium persulphate was used as an oxidant. The produced particles were spherical in shape with an average diameter of 15 nm as detected from the transmittance electron microscope im...
متن کاملSubmicron polyethylene particles from catalytic emulsion polymerization.
Particles of linear polyethylene (M(n) = (2-3) x 10(3) g x mol(-)(1); M(w)/M(n) = 2-4) obtained by catalytic emulsion polymerization of ethylene possess a nonspherical, lentil-like shape with an average aspect ratio of ca. 10 and diameters from 30 to >300 nm, as determined by TEM and AFM. The particle structure results from a stacking of the lamellae along the one shorter axis of the lentils (i...
متن کامل1,2-Polybutadiene Latices by Catalytic Polymerization in Aqueous Emulsion
Catalytic aqueous polymerization of butadiene by the cobalt catalyst system [Co(C8H13)(C4H6)]/CS2 affords colloidally stable latices of highly crystalline syndiotactic 1,2-polybutadiene (Tm ) 190 °C, ∆Hc ) 60 J/g, Mw ∼ 105 g/mol, 97% 1,2, 3% 1,4-cis). Catalyst modification with reagents containing electrophilic carbon atoms (e.g., aromatic formamides) strongly decreases polymer crystallinity (T...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of Polymer Science Part A: General Papers
سال: 1965
ISSN: 0449-2951,1542-6246
DOI: 10.1002/pol.1965.100030627