The Mechanical Alloying Behavior of Fe2O3 into NiO in the High-Energy Ball-Milling Process

The NiO and Fe2O3 powders were mixed by the high-energy ball-milling, followed a sintering of mixture at 1340°C for 0.5 h. XRD, SEM, DSC, size measurements preformed to study microstructure evolution in ball-milled sintered ones, as well. It showed that ball-milling processes resulted severe lattice distortion powder Fe2O3, but only slight NiO. Meanwhile, solid solution iron atoms into was also detected milling process. found solubility delayed synthesizing reaction following