The Leaching Process of Alumina from Red Mud for Synthesis of Mesoporous Alumina
نویسندگان
چکیده
منابع مشابه
Sol-gel synthesis of ordered mesoporous alumina.
Well-ordered mesoporous alumina materials with high surface area and a narrow pore size distribution were synthesized using a sol-gel based self assembly technique.
متن کاملChallenges and Strategies in the Synthesis of Mesoporous Alumina Powders and Hierarchical Alumina Monoliths
A new rapid, very simple and one-step sol-gel strategy for the large-scale preparation of highly porous γ-Al₂O₃ is presented. The resulting mesoporous alumina materials feature high surface areas (400 m² g-1), large pore volumes (0.8 mL g-1) and the γ-Al₂O₃ phase is obtained at low temperature (500 °C). The main advantages and drawbacks of different preparations of mesoporous alumina materials ...
متن کاملMechanochemical synthesis of alumina nanoparticles
Abstract: Nano- size alumina particles have been synthesized by mechanical activation of a dry powder mixture of AlCl3 and CaO. Mechanical milling of the above raw materials with the conditions adopted in this study resulted in the formation of a mixture consisting of crystalline CaO and amorphous aluminum chlorides phases. There was no sign of chemical reaction occurring during milling stag...
متن کاملOrdered mesoporous carbon/α-alumina nanosheet composites.
Novel α-alumina crystalline nanosheets are used for the preparation of alumina-carbon composites, in which the latter component is phenolic resin-based ordered mesoporous carbon. A unique feature of these composites is perpendicular orientation of ordered mesopores of the carbon to the (001) facets of nonporous α-alumina nanosheets accompanied by significant enlargement of these mesopores in co...
متن کاملSucrose synthesis of nanoparticulate alumina
The synthesis of nanoparticulate α-Al 2 O 3 at 600 • C using a sucrose-based polymer dispersion technique was reported recently by Das et al. [1]. This is of interest, as γ-Al 2 O 3 is frequently an unwanted intermediate phase in the conversion of nanoparticulate amorphous alu-mina into nanoparticulate α-Al 2 O 3. γ-Al 2 O 3 has a relatively disordered structure, but usually requires temperatur...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of Physics: Conference Series
سال: 2019
ISSN: 1742-6588,1742-6596
DOI: 10.1088/1742-6596/1351/1/012036