The Kinetic of Al3Ti Phase Growth in Explosively Welded Multilayered Al/Ti Clads during Annealing under Load Conditions
نویسندگان
چکیده
منابع مشابه
THE FORMATION OF TiAl3 DURING HEAT TREATMENT IN EXPLOSIVELY WELDED Ti-Al MULTILAYERS
Metallic-intermetallic laminate (MIL) composites are promising materials for structural applications especially in the aerospace industry. One of the interesting laminate composites is the Ti-TiAl 3 multilayer. In this work, commercially pure sheets of aluminum and titanium with almost equal thickness of around 0.5 mm were explosively joined. The achieved multilayers were annealed at 630 ℃in di...
متن کاملthe effect of taftan pozzolan on the compressive strength of concrete in the environmental conditions of oman sea (chabahar port)
cement is an essential ingredient in the concrete buildings. for production of cement considerable amount of fossil fuel and electrical energy is consumed. on the other hand for generating one tone of portland cement, nearly one ton of carbon dioxide is released. it shows that 7 percent of the total released carbon dioxide in the world relates to the cement industry. considering ecological issu...
the effect of e-64 on the developmental competence of sheep cocs during in vitro maturation
in the present study, the effect of e-64 at different concentrations (0.5, 1, 5 and 10 µm) added to (1) the ivm medium on oocyte nuclear maturation and developmental competence of ovine oocytes, and (2) to the ivc medium on embryonic development of ovine embryos were investigated.
EFFECT OF DIFFUSION ANNEALING ON PROPERTIES OF TI/304L STAINLESS STEEL EXPLOSION CLAD
In this study, commercially pure titanium/304L stainless steel explosion bonded clads have been annealed under argon atmosphere over the temperature range of 700-900°C for 1h.Microstructure of the clads have been investigated before and after anealing. X-ray diffraction studies revealed that the annealing products in the form of intermetallic phases were gradually formed at the interface of the...
متن کاملتشکیل ترکیب بین‌فلزی Al3Ti در فصل مشترک اتصال زوج نفوذی آلومینیوم- تیتانیم از طریق انجام عملیات حرارتی نفوذی
In this study, the formation of the Al3Ti intermetallic compound at the junction interface of aluminum-titanium was investigated during deposition and annealing. The results illustrated that during the deposition process, one thin layer of Ti3Al2 intermetallic compound was created at the junction interface. During the annealing at 550 °C, this layer was transformed to the Al3Ti interm...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Archives of Metallurgy and Materials
سال: 2023
ISSN: ['1733-3490', '2300-1909']
DOI: https://doi.org/10.24425/amm.2019.130125