The Instrumented Indentation Study of HVOF-Sprayed Hardmetal Coatings
نویسندگان
چکیده
منابع مشابه
Instrumented spherical micro-indentation of plasma-sprayed coatings
The mechanical response of plasma-sprayed coatings is studied by recourse to instrumented spherical micro-indentation. It is shown that the elastic moduli of the coatings can be determined in a more reliable and reproducible manner with instrumented spherical indentation than prior (Knoop) indentation methods, while at the same time minimizing damage to the coating during indentation. The resul...
متن کاملThe Study of High Temperature Oxidation behavior of Different Microstructures of HVOF Thermally Sprayed Coatings
Improvement of thermally sprayed coating properties by microstructure modification has been considered as a significant solution. Therefore, in this research the effect of dissolved oxygen content and post heat treatment on the formation and distribution of secondary phase particles, particularly in nano-scale in the coatings during spraying and after that were studied. Ni-5 wt% Al powders were...
متن کاملExperimental and Numerical Study of Residual Stress in the WC-12Co HVOF Sprayed Coatings
Thermally sprayed coatings are intrinsically associated with residual stresses in the deposits. These stresses are varied in nature and magnitude, and have a pronounced effect on the mechanical behavior of the system. In the current study, WC-12Co coatings were deposited using HVOF thermal spraying. The sin2ψ method was used to evaluate the through thickness residual stress by means ...
متن کاملStudy of Wear Behaviour of Hvof and Cold Sprayed Coatings on Boiler Steels
In this study two commonly used steels in boiler plants, i.e. (SAE-213) T-22 and SA516 (Grade-70) were coated with different thermal spray processes namely HVOF and cold spray. The coating powder used was made up of NiCrTiCRe powder. The performance of the coated as well as uncoated material was investigated using a pin-on-disc machine [Model: Wear and Friction Monitor Tester TR-20], supplied b...
متن کاملHot corrosion behavior of HVOF-sprayed CoNiCrAlYSi coatings in a sulphate environment
HVOF-sprayed CoNiCrAlYSi coatings were tested at 900 °C in a hot corrosion environment containing sodium-potassium sulphates. The HVOF spraying caused the typical splat-on-splat structure. The results after the hot corrosion testing showed that the corrosion preferentially occurred at the coating surface and the splat boundaries. The oxidation along the splat boundaries can isolate the splat fr...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of Thermal Spray Technology
سال: 2011
ISSN: 1059-9630,1544-1016
DOI: 10.1007/s11666-011-9677-2