The Influence of Nano-CaCO3 on the Mechanical and Dynamic Thermo-Mechanical Properties of Core–Shell Structured Wood Plastic Composites

نویسندگان

چکیده

Using bamboo residue and high-density polyethylene (HDPE) as the main raw materials, core–shell structured wood plastic composites (WPCs) with nano-CaCO3 filling shell were prepared by coextruded technology. The effect of contents on flexural properties, impact strength dynamic thermo-mechanical properties WPCs investigated. And value interface interaction parameter was calculated thermodynamic parameters. results showed that increased 48.1% 40.3% when it loaded 10%–15% nano-CaCO3, compared to HDPE composites, respectively. While nano-CaCO3-filled had lower in comparison shell, field emission scanning electron microscope revealed proper interfacial adhesion between core layers. storage modulus increased, but values than shell. Addition caused an increase glass transition temperature (Tg) WPCs, loss factor (tan?) decreased. significantly after loading reached 15%, which consistent bending test results. These findings demonstrate have excellent layer, is added layer.

برای دانلود رایگان متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

modification of nanoclay for improving the physico-mechanical properties of dental adhesives

هدف اصلی این مطالعه تهیه یک سامانه نوین چسب عاجی دندانی بر پایه نانورس پیوند شده با پلی متاکریلیک اسید، نانورس پیوند شده با پلی اکریلیک اسید، مخلوط نانوسیلیکا و نانورس پیوند شده با پلی متاکریلیک اسید، مخلوط نانوسیلیکا و نانورس پیوند شده با پلی اکریلیک اسید و نانورس پیوند شده با کیتوسان اصلاح شده با گلایسیدیل متاکریلات است. پیوند پلی متاکریلیک اسید و پلی اکریلیک اسید بر ری سطح نانورس در حضور و ...

Dynamic Mechanical Analysis of Compatibilizer Effect on the Mechanical Properties of Wood Flour-High-Density Polyethylene Composites

In this study, effect of MAPE (maleic anhydride polyethylene) as the compatibilizer on the mechanical properties of wood-flour polyethylene composites has been investigated by using Dynamic Mechanical Analysis (DMA). Composites were made at 25% and 50% by weight fiber contents and 1% and 2% compatibilizer respectively. Controls were also made at the same fiber contents without the compatibilize...

متن کامل

determination of some physical and mechanical properties red bean

چکیده: در این تحقیق، برخی خواص فیزیکی و مکانیکی لوبیا قرمز به-صورت تابعی از محتوی رطوبت بررسی شد. نتایج نشان داد که رطوبت بر خواص فیزیکی لوبیا قرمز شامل طول، عرض، ضخامت، قطر متوسط هندسی، قطر متوسط حسابی، سطح تصویر شده، حجم، چگالی توده، تخلخل، وزن هزار دانه و زاویه ی استقرار استاتیکی در سطح احتمال 1 درصد اثر معنی داری دارد. به طوری که با افزایش رطوبت از 54/7 به 12 درصد بر پایه خشک طول، عرض، ضخام...

15 صفحه اول

Influence of Micro and Nano Silica on Mechanical Properties of Plasticized Sulfur Composites

In this paper the influence of two different sizes of silica particles (micro-silica and nano-silica) was studied on mechanical properties of sulfur and sulfur composite. To improve the structural properties, sulfur was plasticized using dicyclopentadiene (DCPD) and methyl styrene (MSt). Plasticized sulfur composite was prepared by melt blending of plasticized sulfur and silica particles. T...

متن کامل

the influence of the neo-platonic concept of poetic imagination on wordsworth’s poetry

بر اساس نظریه افلاطون در باره شعر خلاقیت هنری مورد انتقاد قرار گرفته است. نظریه کلی در مورد شعر این بود که شعر از ظواهرتقلید میکند و نه حقیقت. چون سایه ای از حقیقت است. اما با پیدایش فلسفه نو افلاطونی، انتقاتات قبلی در مورد شعر و شاعری اصلاح شد. فلوطین در کتاب انئید، اساس خلق هنری را بر محور مُثل افلاطونی قرار داد. وی باور داشت که هنر مندان در خلق آثار هنری، تحت تاثیر مُثل افلاطونی بوده و عوالمی ...

ذخیره در منابع من


  با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید

ژورنال

عنوان ژورنال: Forests

سال: 2023

ISSN: ['1999-4907']

DOI: https://doi.org/10.3390/f14020257