The Fluorescence of Pr3+ in Zinc Lithium Bismuth Borate Glasses with Large Stimulated Emission Cross Section
Glass sample of Zinc Lithium Bismuth Borate (25−x) Bi2O3:20Li2O:20ZnO:35B2O3:xPr6O11, (where x = 1, 1.5 and 2 mol%) has been prepared by melt-quenching technique. The amorphous nature of the prepared glass samples was confirmed by X-ray diffraction. The absorption spectra of three Pr3+ doped zinc lithium bismuth borate glasses have been recorded at room temperature. The observed optical spectra...
متن کاملDoped Zinc Lithium Bismuth Borate Glasses
Zinc lithium bismuth borate glasses containing Er in (25x): Bi2O3:20Li2O:20ZnO: 35B2O3:xEr2O3 (where x=1, 1.5,2 mol %) have been prepared by melt-quenching method. The amorphous nature of the glasses was confirmed by x-ray diffraction studies. Optical absorption and fluorescence spectra were recorded at room temperature for all glass samples. Judd-Ofelt intensity parameters Ωλ (λ=2, 4, 6) are e...
متن کاملions doped zinc bismuth borate glasses
Glasses having composition 20ZnO·xBi2O3·(79-x)B2O3 (15 x 35, in mol%) doped with 1 mol% of Nd 3+ ions were prepared. The different physical and absorption spectral properties have been investigated to understand the variation of the hypersensitive absorption band intensities. From the absorption spectra, Judd-Ofelt intensity parameters, ( = 2, 4, 6) have been calculated and these parameters wer...
متن کاملSynthesis and Characterization of Lithium Borate Glasses Containing Bismuth
A lithium bismuth borate glass system is prepared by the conventional melt quenching technique. The Powder X-Ray diffraction analysis of the prepared samples confirms the amorphous nature of the samples. The density and molar volume studies report the change of structure with the increase of bismuth content. The FTIR analysis of the samples revealed that the network structure of the prepared sa...
متن کاملInfrared broadband emission of bismuth-doped barium-aluminum-borate glasses.
We report near infrared broadband emission of bismuth-doped barium-aluminum-borate glasses. The broadband emission covers 1.3microm window in optical telecommunication systems. And it possesses wide full width at half maximum (FWHM) of ~200nm and long lifetime as long as 350micros. The luminescent properties are quite sensitive to glass compositions and excitation wavelengths. Based on energy m...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: New Journal of Glass and Ceramics
سال: 2016
ISSN: 2161-7554,2161-7562
DOI: 10.4236/njgc.2016.62002