The Fatigue Crack Growth Rate Due to Single-Step Austempered Heat Treatment in Nodular Cast Iron

Fatigue Behaviour of Synthetic Nodular Cast Irons

A. Vaško, L. Trško, R. Konečná, Faculty of Mechanical Engineering, University of Žilina, Žilina, Slovak Republic The paper shows the influence of charge composition on microstructure, fatigue properties and failure micromechanisms of nodular cast irons. The additive of metallurgical silicon carbide (SiC) in analysed specimens increases the content of ferrite in the matrix, decreases the size of...

Fatigue crack growth in a coarse-grained iron–silicon alloy

The fatigue crack growth in a coarse-grained Fe-2 wt% Si alloy is investigated in considerable detail. At room temperature, the material is quasi-brittle and the failure mode is mixed cleavage. Under a mode-I cyclic loading, the crack can overcome the barrier effect of grain boundaries, which dominates the overall damage evolution. Associated with the geometrically necessary crack front branchi...

Effects of Carbides on Fatigue Characteristics of Austempered Ductile Iron

Crack initiation and growth behaviour of an austempered ductile iron (ADI) austenitised at 800C and austempered at 260C has been assessed under three point bend fatigue conditions. Initiation sites have been identified as carbides remaining from the as cast ductile iron due to insufficient austenisation. The number of carbides cracking on loading to stresses greater than 275 MPa is critical in ...

Fatigue Crack Growth Rate Model for Metallic Alloys

A model has been created to allow the quantitative estimation of the fatigue crack growth rate in steels as a function of mechanical properties, test–specimen characteristics, stress–intensity range and test–frequency. With this design, the remarkable result is that the method which is based on steels, can be used without modification, and without any prior fatigue test, to estimate the crack g...

The Effect of Heat Treatment Cycle on Microstructure and Mechanical Properties of Austempered Ductile Iron with Various Copper Contents.