The Effects of Post-Weld Heat Treatment on the Microstructure and Mechanical Properties of 9% Ni Steel Weld Joint with Fe-Based Filler Material

نویسندگان

چکیده

A Fe-based filler material with the composition of Fe-20Ni-5Co-2.5Mn-0.2C was used for welding 9% Ni steel, and effect post-weld heat treatment on microstructure mechanical properties welded joints investigated. Post-weld joint performed in temperature range 200 to 600 ℃. After experimental selection, changes weld metal base were investigated detail at temperatures 350 Grain morphology, size, location precipitated cementite studied using SEM EBSD phase maps. The characterized by tensile micro-hardness. Based results, this study provides key insights into applicability steel prepared improve properties, toughness ductility joints.

برای دانلود باید عضویت طلایی داشته باشید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

Investigation on Effect of Heat Input on the Microstructure and Mechanical Properties of Hadfield Steel Weld Joints in SMAW Process

In this investigation, the effect of heat input of SMAW process on the microstructure and mechanical properties of Hadfield steel weld joints was investigated. For this purpose, 4 annealed sheets with thickness 2 mm prepared from Hadfield steel and then welding applied by SMAW process with 6.75 and 11.25 kJ/mm heat input values. The evaluation of the microstructures of welding joints was condu...

متن کامل

Investigation on Effect of Heat Input on the Microstructure and Mechanical Properties of Hadfield Steel Weld Joints in SMAW Process

In this investigation, the effect of heat input of SMAW process on the microstructure and mechanical properties of Hadfield steel weld joints was investigated. For this purpose, 4 annealed sheets with thickness 2 mm prepared from Hadfield steel and then welding applied by SMAW process with 6.75 and 11.25 kJ/mm heat input values. The evaluation of the microstructures of welding joints was condu...

متن کامل

Effect of Post-weld Heat Treatment on Joint Properties of Dissimilar Friction Stir Welded AA2024 and AA7075 Aluminum Alloys

In present study, the effect of heat treatment after friction stir welding dissimilar welds T6-7075 and T4-2024 aluminum alloys were investigated. Friction stir welding was performed at a constant rotation speed of 1140 rpm and welding speed 32 mm/min. After welding samples are taken under various heat treatment processes at different aging temperature and time period. Microstructural observati...

متن کامل

Effect of Post-weld Heat Treatment on Joint Properties of Dissimilar Friction Stir Welded AA2024 and AA7075 Aluminum Alloys

In present study, the effect of heat treatment after friction stir welding dissimilar welds T6-7075 and T4-2024 aluminum alloys were investigated. Friction stir welding was performed at a constant rotation speed of 1140 rpm and welding speed 32 mm/min. After welding samples are taken under various heat treatment processes at different aging temperature and time period. Microstructural observati...

متن کامل

Influence of Post-Weld Heat Treatment on the Microstructure, Microhardness, and Toughness of a Weld Metal for Hot Bend

In this work, a weld metal in K65 pipeline steel pipe has been processed through self-designed post-weld heat treatments including reheating and tempering associated with hot bending. The microstructures and the corresponding toughness and microhardness of the weld metal subjected to the post-weld heat treatments have been investigated. Results show that with the increase in reheating temperatu...

متن کامل

ذخیره در منابع من


  با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید

ژورنال

عنوان ژورنال: Korean Journal of Metals and Materials

سال: 2023

ISSN: ['1738-8228', '2288-8241']

DOI: https://doi.org/10.3365/kjmm.2023.61.9.669